Comparison between the effects of phosphorous slag and fly ash on the C-S-H structure, long-term hydration heat and volume deformation of cement-based materials
Tóm tắt
Từ khóa
Tài liệu tham khảo
Jung, 2017, Use of ternary blended concrete to mitigate thermal cracking in massive concrete structures-A field feasibility and monitoring case study, Constr. Build. Mater., 137, 208, 10.1016/j.conbuildmat.2017.01.108
Li, 2014, A numerical simulation of the temperature cracking propagation process when pouring mass concrete, Automat. Constr., 37, 203, 10.1016/j.autcon.2013.08.005
Yen, 2007, Influence of class F fly ash on the abrasion–erosion resistance of high-strength concrete, Constr. Build. Mater., 21, 458, 10.1016/j.conbuildmat.2005.06.051
Oner, 2005, An experimental study on strength development of concrete containing fly ash and optimum usage of fly ash in concrete, Cem. Concr. Res., 35, 1165, 10.1016/j.cemconres.2004.09.031
Hu, 2017, Comparison between the effects of superfine steel slag and superfine phosphorus slag on the long-term performances and durability of concrete, J. Therm. Anal. Calorim., 128, 1251, 10.1007/s10973-017-6107-9
Walkley, 2019, NMR Solid-state nuclear magnetic resonance spectroscopy of cements, Mater. Today, 1
Bouchenafa, 2019, PCA effect on structure of fly ashes and slag obtained by mechanosynthesis. Applications: Mechanical performance of substituted paste CEMI + 50% slag/or fly ashes, Constr. Build. Mater., 203, 120, 10.1016/j.conbuildmat.2019.01.063
Hamzaoui, 2016, The sequel of modified fly ashes using high energy ball milling on mechanical performance of substituted past cement, Mater. Design, 90, 29, 10.1016/j.matdes.2015.10.109
Siddique, 2011
Wongkeo, 2012, Compressive strength and drying shrinkage of fly ash-bottom ash-silica fume multi-blended cement mortars, Mater. Des., 36, 655, 10.1016/j.matdes.2011.11.043
Altoubat, 2017, Effectiveness of fly ash on the restrained shrinkage cracking resistance of self-compacting concrete, Cem. Conc. Compos., 79, 9, 10.1016/j.cemconcomp.2017.01.010
Kristiawan, 2015, Effect of high volume fly ash on shrinkage of self-compacting concrete, Procedia Eng., 125, 705, 10.1016/j.proeng.2015.11.110
Wang, 2017, Effect of silica fume and PVA fiber on the abrasion resistance and volume stability of concrete, Compos. Part B-Eng., 130, 28, 10.1016/j.compositesb.2017.07.058
Atis, 2002, Heat evolution of high-volume fly ash concrete, Cem. Concr. Res., 32, 751, 10.1016/S0008-8846(01)00755-4
Ha, 2014, Thermal crack control in mass concrete structure using an automated curing system, Automat. Constr., 45, 16, 10.1016/j.autcon.2014.04.014
Wang, 2018, Mechanical properties, long-term hydration heat, shinkage behavior and crack resistance of dam concrete designed with low heat Portland (LHP) cement and fly ash, Constr. Build. Mater., 187, 1073, 10.1016/j.conbuildmat.2018.08.056
Yin, 2018, Investigation of the hydration kinetics and microstructure formation mechanism of fresh fly ash cemented filling materials based on hydration heat and volume resistivity characteristics, Applied Clay Sci., 166, 146, 10.1016/j.clay.2018.09.019
Termkhajornkit, 2005, Effect of fly ash on autogenous shrinkage, Cem. Concr. Res., 35, 473, 10.1016/j.cemconres.2004.07.010
Hu, 2017, Early age shrinkage and heat of hydration of cement-fly ash-slag ternary blends, Constr. Build. Mater., 153, 857, 10.1016/j.conbuildmat.2017.07.138
Liao, 2004, A study on characteristics of interfacial transition zone in concrete, Cem. Concr. Res., 34, 977, 10.1016/j.cemconres.2003.11.019
Poon, 2000, A study on high strength concrete prepared with large volumes of low calcium fly ash, Cem. Concr. Res., 30, 447, 10.1016/S0008-8846(99)00271-9
Moghaddam, 2019, The effect of fly ash fineness on heat of hydration, microstructure, flow and compressive strength of blended cement pastes, Case Studies in Constr. Mater., 10
Peng, 2017, Study of the key technologies of application of tuff powder concrete at the Daigo hydropower station in Tibet, Constr. Build. Mater., 156, 1, 10.1016/j.conbuildmat.2017.08.138
Yang, 2019, Low carbon design of an ultra-high performance concrete (UHPC) incorporating phosphorous slag, J. Clean. Prod., 240, 10.1016/j.jclepro.2019.118157
Li, 2015, The status quo analysis and policy suggestions on promoting China׳s hydropower development, Renew. Sust. Energ. Rev., 51, 1071, 10.1016/j.rser.2015.07.044
He, 2019, The investigation of early hydration and pore structure for limestone powder wastes blended cement pastes, J. Therm. Anal. Calorim., 229
Chen, 2009, Anti-crack performance of phosphorus slag concrete, J. Wuhan Univ. Technol.-Mater. Sci. Ed., 14, 80, 10.1007/s11859-009-0117-9
Allahverdi, 2016, Influence of curing conditions on the mechanical and physical properties of chemically-activated phosphorous slag cement, Powder Technol., 288, 132, 10.1016/j.powtec.2015.10.053
Peng, 2015, Properties and microstructure of reactive powder concrete having a high content of phosphorous slag powder and silica fume, Constr. Build. Mater., 101, 482, 10.1016/j.conbuildmat.2015.10.046
Wang, 2017, Influence of high-volume electric furnace nickel slag and phosphorous slag on the properties of massive concrete, J. Therm. Anal. Calorim., 131, 873, 10.1007/s10973-017-6576-x
Allahverdi, 2013, Mechanical activation of chemically activated high phosphorous slag content cement, Powder Technol., 245, 182, 10.1016/j.powtec.2013.04.037
Li, 2000, The influence of admixtures on the properties of phosphorous slag cement, Cem. Concr. Res., 30, 1169, 10.1016/S0008-8846(00)00291-X
Yang, 2020, Shrinkage properties and microstructure of high volume ultrafine phosphorous slag blended cement mortars with superabsorbent polymer, J. Build. Eng., 52
Chen, 2011, Hydration kinetics of phosphorus slag-cement paste, J. Wuhan Univ. Technol. - Mater. Sci. Ed., 26, 142, 10.1007/s11595-011-0186-4
Mehdizadeh, 2018, Rheology and apparent activation energy of alkali activated phosphorous slag, Constr. Build. Mater., 171, 197, 10.1016/j.conbuildmat.2018.03.130
Shi, 1989, Investigation on some factors affecting the characteristics of alkali-phosphorus slag cement, Cem. Concr. Res., 19, 527, 10.1016/0008-8846(89)90004-5
Allahverdi, 2014, Resistance of chemically-activated high phosphorous slag content cement against freeze–thaw cycles, Cold Reg. Sci. Technol., 103, 107, 10.1016/j.coldregions.2014.03.012
JC/T 740-2006. Portland phosphorous slag cement, China, China Building Materials Industry Press, Beijing.
Gao, 2008, Microstructure and pore structure of concrete mixed with superfine phosphorous slag and superplasticizer, Constr. Build. Mater., 22, 837, 10.1016/j.conbuildmat.2006.12.015
Zhang, 2017, Hydration mechanisms of composite binders containing phosphorus slag at different temperatures, Constr. Build. Mater., 147, 720, 10.1016/j.conbuildmat.2017.04.202
Sun, 2006, The role of Al in C-S-H: NMR, XRD, and compositional results for precipitated samples, Cem. Concr. Res., 36, 18, 10.1016/j.cemconres.2005.03.002
Malek, 2005, The contribution of class-F fly ash to the strength of cementitious mixtures, Cem. Concr. Res., 35, 1152, 10.1016/j.cemconres.2004.10.021
Zhang, 2017, Novel understanding of calcium silicate hydrate from dilute hydration, Cem. Concr. Res., 99, 95, 10.1016/j.cemconres.2017.04.016
L’Hôpital, 2015, Incorporation of aluminium in calcium-silicate-hydrates, Cem. Concr. Res., 75, 91, 10.1016/j.cemconres.2015.04.007
GB 175-2007. Common Portland cement, China, China Standard Press, Beijing.
ASTM C618. Standard specification for coal fly ash and raw or calcined natural pozzolan, West Conshohocken (PA): ASTM International, 2012.
GB/T 1596-2017. Fly ash used for cement and concrete, China, China Standard Press, Beijing.
GB/T 8074-2008. Testing method for specific surface of cement-Blaine method, China, China Standard Press, Beijing.
DL/T 5387-2007. Technical specification for phosphorous slag powder use in hydraulic concrete, China, China Electric Power Press, Beijing.
DL/T 5151-2014. Code for testing aggregates of hydraulic concrete, China, China Electric Power Press, Beijing.
DL/T 5144-2015. Specifications for hydraulic conrete construction, China, China Electric Power Press, Beijing.
SL 191-2008. Design code for hydraulic concrete structures, China, China Water Conservancy and Hydropower Press, Beijing.
DL/T 5330-2015. Code for mix design of hydraulic concrete, China, China Electric Power Press, Beijing.
Kim, 2018, Slag waste incorporation in high early strength concrete as cement replacement: Environmental impact and influence on hydration & durability attributes, J. Clean. Prod., 172, 3056, 10.1016/j.jclepro.2017.11.105
Yang, 2016, Influence study of extra-large stone limited size and content on full-graded concrete properties, Constr. Build. Mater., 127, 774, 10.1016/j.conbuildmat.2016.10.006
Schneider, 2001, 29Si and 27Al high-resolution NMR characterization of calcium silicate hydrate phases in activated blast-furnace slag pastes, Cem. Concr. Res., 31, 993, 10.1016/S0008-8846(01)00530-0
C. MD., G. Goberdhan., 29Si MAS NMR study of the hydration of tricalcium silicate in the presence of finely divided silica, J. Mater. Sci. 23(11) (1988) 4108-4114.
GB, T,, 2008
DL/T5150-2017, Test code for hydraulic concrete, China, China Electric Power Press, Beijing.
Deboodt, 2016, Evaluation of FLWA and SRAs on autogenous deformation and long-term drying shrinkage of high performance concrete, Constr. Build. Mater., 119, 53, 10.1016/j.conbuildmat.2016.05.068
Zhang, 2017, Study on microstructure and bond strength of interfacial transition zone between cement paste and high-performance lightweight aggregates prepared from ferrochromium slag, Constr. Build. Mater., 142, 31, 10.1016/j.conbuildmat.2017.03.083
Rashad, 2014, Effect of silica fume and slag on compressive strength and abrasion resistance of HVFA concrete, Int. J. Concr. Struct. M., 8, 69, 10.1007/s40069-013-0051-2
Ma, 2016, Influence of nano-TiO2 on physical and hydration characteristics of fly ash–cement systems, Constr. Build. Mater., 122, 242, 10.1016/j.conbuildmat.2016.02.087
Chen, 2011, Characterization of mortars from belite-rich clinkers produced from inorganic wastes, Cem. Conc. Compos., 33, 261, 10.1016/j.cemconcomp.2010.10.012
Martínez-Ramírez, 2019, Pozzolanic reaction of a biomass waste as mineral addition to cement based materials: studies by nuclear magnetic resonance (NMR), Int. J. Concr. Struct. M., 13, 1
Roncero, 2002, Study of the influence of superplasticizers on the hydration of cement paste using nuclear magnetic resonance and X-ray diffraction techniques, Cem. Concr. Res., 32, 103, 10.1016/S0008-8846(01)00636-6
Yang, 2019, Eco-friendly treatment of low-calcium coal fly ash for high pozzolanic reactivity: A step towards waste utilization in sustainable building material, J. Clean. Prod., 238, 10.1016/j.jclepro.2019.117962
Bernal, 2013, Gel nanostructure in alkali-activated binders based on slag and fly ash, and effects of accelerated carbonation, Cem. Concr. Res., 53, 127, 10.1016/j.cemconres.2013.06.007
Liu, 2018, Effects of nano-SiO2 on early strength and microstructure of steam-cured high volume fly ash cement system, Constr. Build. Mater., 194, 350, 10.1016/j.conbuildmat.2018.10.214
ASTM C311/C311M-17. Standard test methods for sampling and testing fly ash or natural pozzolans for use in Portland-cement concrete.
Foley, 2012, Synthesis and nano-mechanical characterization of calcium-silicate-hydrate (C-S-H) made with 1.5CaO/SiO2 mixture, Cem. Concr. Res., 42, 1225, 10.1016/j.cemconres.2012.05.014
Singh, 2016, Studies on early stage hydration of tricalcium silicate incorporating silica nanoparticles: Part II, Constr. Build. Mater., 102, 943, 10.1016/j.conbuildmat.2015.05.084
Liu, 2016, Effect of waste gypsum on the setting and early mechanical properties of belite-C2.75B1.25A3$ cement, J. Therm. Anal. Calorim., 125, 75, 10.1007/s10973-016-5265-5
Sun, 2017, Effects of synthetic C-S-H/PCE nanocomposites on early cement hydration, Constr. Build. Mater., 140, 282, 10.1016/j.conbuildmat.2017.02.075
da Costa, 2016, Production and hydration of calcium sulfoaluminate-belite cements derived from aluminium anodising sludge, Constr. Build. Mater., 122, 373, 10.1016/j.conbuildmat.2016.06.022
Deschner, 2012, Hydration of Portland cement with high replacement by siliceous fly ash, Cem. Concr. Res., 42, 1389, 10.1016/j.cemconres.2012.06.009
Sakai, 2005, Hydration of fly ash cement, Cem. Concr. Res., 35, 1135, 10.1016/j.cemconres.2004.09.008
Termkhajornkit, 2006, Effect of water curing conditions on the hydration degree and compressive strengths of fly ash–cement paste, Cem. Conc. Compos., 28, 781, 10.1016/j.cemconcomp.2006.05.018
Panesar, 2017, Effect of cement type and limestone particle size on the durability of steam cured self-consolidating concrete, Cem. Conc. Compos., 80, 175, 10.1016/j.cemconcomp.2017.03.007
Shafiq, 2011, Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system, Ksce J. Civil Eng., 15, 1253, 10.1007/s12205-011-1193-x
Abdelrazig, 1989, Estimation of the degree of hydration in modified ordinary portland cement pastes by differential scanning calorimetry, Thermochim. Acta, 145, 203, 10.1016/0040-6031(89)85140-8
Mindess, 2002
Sabine, 2003, Influence of aggregates on chloride diffusion coefficient into mortar, Cem Concr Res, 33, 1021, 10.1016/S0008-8846(03)00009-7
Sun, 2011, Multi-scale prediction of the effective chloride diffusion coefficient of concrete, Constr. Build. Mater., 25, 3820, 10.1016/j.conbuildmat.2011.03.041
Zhang, 2016, Hydration of cement and pore structure of concrete cured in tropical environment, Cem. Concr. Res., 36, 1947, 10.1016/j.cemconres.2004.11.006
Golewski, 2018, An assessment of microcracks in the interfacial transition zone of durable concrete composites with fly ash additives, Compos. Struct., 200, 515, 10.1016/j.compstruct.2018.05.144
Richardson, 1999, The nature of C-S-H in hardened cements, Cem. Concr. Res., 29, 1131, 10.1016/S0008-8846(99)00168-4
Jiang, 2020, Utilization of limestone powder and fly ash in blended cement: Rheology, strength and hydration characteristics, Constr. Build. Mater., 232, 10.1016/j.conbuildmat.2019.117228
Ma, 2018, Effect of triisopropanolamine on compressive strength and hydration of cement-fly ash paste, Constr. Build. Mater., 179, 89, 10.1016/j.conbuildmat.2018.05.117
L’Hôpital, 2016, Influence of calcium to silica ratio on aluminium uptake in calcium silicate hydrate, Cem. Concr. Res., 85, 111, 10.1016/j.cemconres.2016.01.014
F. Ana, A.G.d.l. Torre, A. Palomo, G. López-Olmo, M.M. Alonso, M.A.G. Aranda, Quantitative determination of phases in the alkaline activation of fly ash. Part II: Degree of reaction, Fuel 85(14) (1996) 1960-1969.
Zhang, 2000, Hydration of high-volume fly ash cement pastes, Cem. Conc. Compos., 22, 445, 10.1016/S0958-9465(00)00044-5
Zou, 2020, Enhancement of early-age strength of the high content fly ash blended cement paste by sodium sulfate and C-S-H seeds towards a greener binder, J. Clean. Prod., 224
Wu, 2003, The macro- and micro properties of cement pastes with silica-rich materials cured by wet-mixed steaming injection, Cem. Concr. Res., 33, 1331, 10.1016/S0008-8846(03)00059-0
Tang, 2014, Characterization of early-age hydration process of cement pastes based on impedance measurement, Constr. Build. Mater., 68, 491, 10.1016/j.conbuildmat.2014.07.009
Kalina, 2016, Effect of Na3PO4 on the hydration process of alkali-activated blast furnace slag, Materials, 9, 395, 10.3390/ma9050395
Codina, 2008, Design and characterization of low-heat and low-alkalinity cements, Cem. Concr. Res., 38, 437, 10.1016/j.cemconres.2007.12.002
Halse, 1984, Development of microstructure and other properties in flyash OPC systems, Cem. Concr. Res., 14, 491, 10.1016/0008-8846(84)90124-8
He, 1984, Hydration of fly ash-portland cements, Cem. Concr. Res., 14, 505, 10.1016/0008-8846(84)90126-1
Langan, 2002, Effect of silica fume and fly ash on heat of hydration of Portland cement, Cem. Concr. Res., 32, 1045, 10.1016/S0008-8846(02)00742-1
Lung, 1991, The effects of blast-furnace slag and fly ash on the hydration of portland cement, Cem. Concr. Res., 21, 410, 10.1016/0008-8846(91)90090-5
Zhu, 2014
Ferraris, 2001, The influence of mineral admixtures on the rheology of cement paste and concrete, Cem. Concr. Res., 31, 245, 10.1016/S0008-8846(00)00454-3
Siddique, 2004, Performance characteristics of high-volume Class F fly ash concrete, Cem. Concr. Res., 34, 487, 10.1016/j.cemconres.2003.09.002
Chindaprasirt, 2005, Effect of fly ash fineness on compressive strength and pore size of blended cement paste, Cem. Conc. Compos., 27, 425, 10.1016/j.cemconcomp.2004.07.003
Ma, 2015, The shrinkage of alkali activated fly ash, Cem. Concr. Res., 68, 75, 10.1016/j.cemconres.2014.10.024
Tongaroonsri, 2009, Effect of mineral admixtures and curing periods on shrinkage and cracking age under restrained condition, Constr. Build. Mater., 23, 1050, 10.1016/j.conbuildmat.2008.05.023
Hawreen, 2018, On the mechanical and shrinkage behavior of cement mortars reinforced with carbon nanotubes, Constr. Build. Mater., 168, 459, 10.1016/j.conbuildmat.2018.02.146
Rao, 2001, Long-term drying shrinkage of mortar-influence of silica fume and size of fine aggregate, Cem. Concr. Res., 31, 171, 10.1016/S0008-8846(00)00347-1
Hu, 2017, Drying shrinkage and cracking resistance of concrete made with ternary cementitious components, Constr. Build. Mater., 149, 406, 10.1016/j.conbuildmat.2017.05.113
Yang, 2017, Influence of fly ash on the pore structure and shrinkage characteristics of metakaolin-based geopolymer pastes and mortars, Constr. Build. Mater., 153, 284, 10.1016/j.conbuildmat.2017.05.067
Zhang, 2003, Effect of water-to-cementitious materials ratio and silica fume on the autogenous shrinkage of concrete, Cem. Concr. Res., 33, 1687, 10.1016/S0008-8846(03)00149-2
Nath, 2011, Effect of fly ash on the durability properties of high strength concrete, Procedia Eng., 14, 1149, 10.1016/j.proeng.2011.07.144