Combustion synthesis of PZN-10PT nanopowders
Tóm tắt
Discussed is the influence of the fuel and water employed in combustion synthesis of single-phase (perovskite) PZN-10PT nanopowder with an x = 0.10 composition. Pb(NO3)2, Zn(NO3)2 · 6H2O, (NH4NbO(C2O4)2), and C8H20O4Ti were used as cation precursors while urea, glycine, glycine/urea (50/50 ratio), and tetraformal triazine (TFTA), as fuels. Two sets of precursors (denoted as set-1 and set-2) were used with each of these fuels, and four different fuels: without and with the addition of 250 mL of water. The results indicated that the highest percentage of perovskite phase in the PZN-10PT nanopowders was obtained using an urea/glycine mixture as a fuel. When the urea/glycine mixture was added to the solution containing cations precursors, the two fuels form a gel in aqueous solution, this gel contributes not only to obtain homogeneously mixed in the starting material but also aids explosive combustion leading to a high-temperature reaction within a shorter period of time, which is a condition that favors the formation of metastable PZN-10PT nanopowders.
Tài liệu tham khảo
Cross, L.E., Relaxor Ferroelectrics, Ferroelectrics, 1987, vol. 76, pp. 241–247.
Cox, D.E., Noheda, B. and Shirane, G., Universal Phase Diagram for High-Piezoelectric Perovskite Systems, Appl. Phys. Lett., 2001, vol. 79, p. 400.
Kuwata, K., Uchino, M., and Nomura, S., Diffuse Phase Transition in Lead of 0.91Pb(Zn3Nb2O3)-09PbTiO3 Single Crystals. Jpn. J. Appl. Phys., 1982, vol. 2, pp. 1298–1302.
Werde, K., Vanhoyland, G., Nelis, D., Mondelaers, D., van Bael, M.K., Mullens, J., and van Poucke, L.C., Phase Formation of Ferroelectric Perovskite (1 − x)Pb(Zn1/3Nb2/3)O3 − x BaTiO3 by Use of Aqueous Sol-Gel Chemistry, J. Mater. Chem., 2001, vol. 1, pp. 1192–1197.
Jan, H.M., Oh, S.H., and Moon, J.H., Thermodynamic Stability and Mechanisms of Formation and Decomposition of the Perovskite Pb(Zn1/3Nb2/3)O3 Prepared by the PbO Flux Method, J. Amer. Ceram. Soc., 1992, vol.75, pp. 82–88.
Gururaj, T.R., Safari, A., and Halliyal, A., Preparation of PZN-PT Ceramic Powder near the Morphotropic Phase Boundary, Am. Ceram. Soc. Bull., 1986, vol. 65, pp. 1601–1603.
Algueró, M., Ricote, J., and Castro, A., Mechanosynthesis and Thermal Stability of Piezoelectric Perovskite 0.92Pb(Zn1/3Nb2/3)O3-0.08PbTiO3 Powders, J. Am. Ceram. Soc., 2004, vol. 87, pp. 772–778.
Yun, S. and Wang, X., Preparation of PZN-PT-BT Ferroelectric Ceramics by Modified Two-Step Method, Mater. Chem. Phys., 2006, vol. 98, pp. 62–65.
Lian, C. et al., Fabrication and Electric Properties of PZN-Based Ceramics Using Modified Columbite Method, J. Eur. Ceram. Soc., 2006, vol. 25, pp. 2197–2200.
Brankovic, Z., Brankovic, G., and Arana, J.A., PZT Ceramics Obtained from Mechanochemically Synthesized Powders, J. Mater. Sci. Mater. Electron., 2003, vol. 14, pp. 37–41.
Mirtes, M., Paula, C.C. de, Garcia, D., Kiminami, R.H.G.A., Eiras, J.A., and Mascarenhas, Y.P., Microstructural Characterization Using the Rietveld Method in Lead Lanthanum Titanate Ceramics System Produced by Combustion Synthesis, J. Eur. Ceram. Soc., 2007, vol. 27, pp. 3719–3721.
Yi, J.H., Thomas, M., Manier, J.P., Mercurio, Jauberteau, I., Guinebretiere, R., et al., SrBi2Nb2O9 Ferroelectric Powders and Thin Films Prepared by Sol-Gel, J. Sol-Gel Sci. Technol., 1998, vol. 13, pp. 885–888.
Wen, H., Wang, X.H., and Li, L.T., Fabrication and Properties of Sol-Gel-Derived BiScO3-PbTiO3 Thin Films, J. Am. Ceram. Soc., 2006, vol. 89, pp. 2345–2347.
Wang J. et al., Synthesizing Nanocrystalline Pb(Zn1/3Nb2/3)O3 Powders from Mixed Oxides, J. Amer. Ceram. Soc., 1999, vol. 82, pp. 477–479.
Paula, C.C. de, Nascente, P.A.P., Eiras, J.A., Garcia, D., and Kiminami, R.H.G.A., Surface and Microstructural Characterization of Lanthanum Modified Lead Titanate Obtained by Combustion Synthesis, Ferroelectrics, 2006, vol. 348, pp. 187–195.
Costa, A.C.F.M, Morelli, M.R., and Kiminami, R.H.G.A., Combustion Synthesis Processing of Nanoceramics, Handbook of Nanoceramics and Their Based Nanodevices, 2009, vol. 1, pp. 375–391.
Raigoza, C.F.V., Influência dos Parâmetros de Síntese e de Processamento na Formação e Estabilização da Fase Perovskita no Sistema Cerâmico 0.90PZN-0.10PT, PhD Thesis, Universidade Federal de São Carlos, Brazil, 2007.
Kiminami, R.H.G.A., Combustion Synthesis of Nanopowder Ceramic Powders, KONA, 2001, vol. 19, pp. 156–165.
Barros, B.S., Kiminami, R.H.G.A., Costa, A.C.F.M., Alves, J.R., Sá, G.F. de, Photophysical Properties of Eu3+ and Tb3+ Doped ZnAl2O4 Phosphors Obtained by Combustion Reaction, J. Mater. Sci., 2006, vol. 41, pp. 4744–4748.
Sekar, M.A., Halliyal, A., and Patil, K.C., Synthesis, Characterization, and Properties of Lead-Based Relaxor Ferroelectrics, J. Mater. Res., 1996, vol. 11, pp. 1210–1218.
Sekar, M.A. and Halliyal, A., Low-Temperature Synthesis, Characterization, and Properties of Lead-Based Ferroelectric Niobates, J. Am. Ceram. Soc., 1998, vol. 81, pp. 380–388.
Jang, J.M., Oh, S.H., and Moon, J.H.J., Thermodynamic Stability and Mechanisms of Formation and Decomposition of Perovskite Pb(Zn1/3Nb2/3)O3 Prepared by the PbO Flux Method, J. Am. Ceram. Soc., 1992, vol. 75, pp. 82–88.
Klung, H. and Alexander, L., X-Ray Diffraction Procedures, New York: Wiley, 1962.
Wakiya, N. et al., Thermal Stability of Pb(Zn1/3Nb2/3)O3 (PZN) and Consideration of Stabilization Conditions of Perovskite Type Compounds, Mater. Res. Bull., 1995, vol. 30, pp. 1121–1131.