Characterization of a modified silicon-containing arylacetylene resin with POSS functionality
Tóm tắt
A modified silicon-containing arylacetylene resin with a well-defined organic-inorganic POSS functionality was successfully synthesized by Huisgen azide-alkyne 1,3-dipolar cycloaddition. The POSS hybridized resin exhibits excellent thermal properties which were characterized by differential scanning calorimetry (DSC) and thermogravimetric analyses (TGA). Scanning electron microscope (SEM) was used to characterize fracture surface of the hybridized polymer. The results show that phase separation occurs. The POSS moieties are aggregated each other in the polymer to form 200–400 nm domains.
Tài liệu tham khảo
Itoh, M., Inoue, K., Iwata, K., Mitsuzuka, M. and Kakigano, T., Macromolecules, 1997, 30: 694
Buvat, P., Jousse, F., Delnaud, L. and Levassort, C., International SAMPE Symposium and Exhibition, 2001, 46: 134
Zhang, J., Huang, J., Zhou, W., Huang, F. and Du, L., eXPRESS Polymer Letter, 2007, 1(12): 831
Phillips, S.H., Haddad, T.S. and Tomczak, S.J., Curr. Opin. Solid State Mater. Sci., 2004, 29: 821
Haddad, T.S. and Lichtenhan, J.D., Macromolecules, 1996, 29(22): 7302
Haddad, T.S., Oviatt, H.W., Schwab, J.J., Mather, P.T., Chaffee, K.P. and Lichtenhan, J.D., Polym. Prepr. (Am. Chem. Soc. Div. Polym. Chem.), 1998, 39: 611
Mather, P.T., Jeon, H.G. and Uribe, A.R., Macromolecules, 1999, 32(4): 1194
Tsuchida, A., Bolln, C., Sernetz, F.G., Frey, H. and Mulhaupt, R., Macromolecules, 1997, 30(10): 2818
Lee, A. and Lichtenhan, J.D., Macromolecules, 1998, 31: 4970
Zhang, X.J., Han, X.N., Fang, S.M., Li, Y.D., Zhang, Z.H. and Yan, C.M., Acta Polymerica Sinica(in Chinese), 2010, (8): 1023
Liu, L., Wang, W.P., Jie, X.X., Gao, H.M. and Fei, M., Acta Polymerica Sinica(in Chinese), 2010, (1): 10
Hu, Y.H., Luo, Y.H., Wan, L.Q., Qi, H.M., Huang, F.R. and Du, L., Acta Polymerica Sinica(in Chinese), 2005, (4): 560
Tian, J.J., Wan, L.Q., Huang, J.Z., Hu, Y.H., Huang, F.R. and Du, L., Polym. Adv. Technol., 2007, 18: 556
Qin, A.J., Jim, C.K.W., Lam, J.W.Y., Sun, J.Z. and Tang, B.Z., Chinese J. Polym. Sci., 2010, 27(2): 145
Liu, S.L., H, Y.H., Seng, S.J., Huang, F.R. and Du, L., Chemical Reagents, 2005, 27(1): 39
Yan, H., Qi, H.M. and Huang, F.R., Petrochemical Technology(in Chinese), 2004, 33(9): 880
Ni, Y. and Zheng, S.X., J. Polym. Sci. Part A: Polym. Chem., 2007, 45: 1247