Changes in composition and characteristics of latex paints applied on porous inorganic substrates
Tóm tắt
Changes in film composition and characteristics that occur during and/or immediately after the application of latex paints on porous inorganic substrates were investigated. Gas chromatography (GC) and thermal analysis were among the techniques used for this purpose. The changes in coalescing agent and binder content were determined by GC and thermogravimetric-analysis, respectively, and the changes in glass transition temperature by differential scanning calo rimetry. It was found that the type of porous substrate could significantly affect the paint composition (pigment volume concentration, coalescent level) during the film formation process.
Tài liệu tham khảo
Scheidegger, A.E.,The Physics of Flow Through Porous Media, University of Toronto Press, 1974.
Gérard, R., et al., CSTC/WTCB Notes d’information Technique, No. 146, 1983/04;CSTC/WTCB Magazine, 3, 12 (1996).
Kleive, K., “Weathered Wooden Surfaces—Their Influence on the Durability of Coating Systems,”Journal of Coatings Technology,58, No. 741, 39 (1986).
Williams, R.S., et al., “Paint Adhesion to Weathered Wood,”Journal of Coatings Technology,59, No. 749, 43 (1987);
Williams, R.S. and Feist, W.C., “Effect of Preweathering, Surface Roughness and Wood Species on the Performance of Paints and Stains,”Journal of Coatings Technology,66, No. 828, 109 (1994).
Hofland, A., “Water-borne Coatings for Decorative and Protective Coatings: A Comparative Survey,”Sur. Coat. Int., 7, 270 (1994).
de Meijer, M., Interactions Between Wood and Coatings with Low Organic Solvent Content, Ph.D. Thesis, Wageningen University, The Netherlands, 1999.
Twenty-eight papers in 3rd International Congress on Polymers in Concrete, Koriyama, Japan, vol. 2, 1981.
Stanfield, R.F., “Protective Coatings for Concrete,”J. Oil & Colour Chemists’ Assoc., 4, 150 (1989).
Hoy, K.L., “Estimating Effectiveness of Latex Coalescing Aids,”Journal of Paint Technology,45, No. 579, 51 (1973).
Winnik, M.A., Wang, Y., and Haley, F.J., “Latex Film Formation at the Molecular Level: The Effect of Coalescing Aids on Polymer Diffusion,”Journal of Coatings Technology,64, No. 811, 51 (1992).
Provder, T., Winnik, M.A. and Urban M.W., (Eds.),Film Formation in Waterborne Coatings, ACS Symposium Series 648, 1996.
Nine papers inProg. Org. Coat., 30, No. 3 (1997).
Perera, D.Y. and Vanden Eynde, D., “Effect of Pigmentation on Internal Stress in Latex Coatings,”Journal of Coatings Technology,56, No. 717, 47 (1984).
Perera, D.Y., “Stress Phenomena in Organic Coatings” (Chapter 49). InPaint and Coating Testing Manual, 14th Edition of the Gardener-Sward Handbook, Koleske, J.V. (Ed.), ASTM, MNL 17, 585, 1995.
Nielsen, L.A.,Mechanical Properties of Polymers and Composites, Vol. 1 and 2, Marcel Dekker Inc., NY, 1974.
Toussaint, A., “Influence of Pigmentation on the Mechanical Properties of Paint Films,”Prog. Org. Coat., 2, 237 (1973/1974).
Zosel, A., “Mechanical Behaviour of Coating Films,”Prog. Org. Coat., 8, 47 (1980).
Perera, D.Y. and Selier, P., “Water Transport in Organic Coatings,”Prog. Org. Coat., 2, No. 1, 57 (1973).