Carbide morphology in p/m IN-792
Tóm tắt
Adequate tensile and smooth stress rupture properties were achieved by heat treating p/m IN-792 to produce serrated grain boundaries pinned with a globular M23C6 precipitate. A notch-strengthened condition with Kt = 3.5 at 1400‡F (1033 K)/90 ksi (620 MN/m2) was achieved when the material was heat treated to produce a grain size larger than about 76 Μm (ASTM G.S. #6). To obtain this grain size using realistic solution time-temperature heat treatments, the carbon content of the IN-792 should be maintained below 0.1 pct and preferably about 0.04 pct.
Tài liệu tham khảo
J. M. Larson: “P/M IN-100-Processing, Microstructures and Mechanical Properties,≓Modern Developments in P/M, vol. 8, p. 537, 1973 International Powder Metallurgy Conference, 1974.
J. C. Freche, W. J. Walters, and R. L. Ashbrook: NASA TN D5248, March, 1969.
G. I. Friedman and P. Loewenstein: AFML-TR-68-321, October, 1968.
P. S. Kotval: NASA CR-72644, December, 1969.
G. I. Friedman:The Powder Metallurgy at Five Nickel Superalloys, Whittaker College Nuclear Metals Division, W. Concord, Mass., January, 1971.
J. F. Barker and E. H. VanDerMulen:Superalloys-Processing, MCIC-72-10, Section A-A, September, 1972.
L. R. Woodyatt, C. T. Sims, and H. J. Beattie,:Trans. TMS-AIME, 1966, vol. 236, p. 519.
K. E. Burke:Metallography, 1975, vol. 8, no. 6, p. 473.
M. J. Donachie, and O. H. Kriege:J. Mater., 1972, vol. 1, p. 269.
J. L. Hague, E. D. Brown, and H. A. Bright:J. Res. Nat. Bur. Stand., October, 1954, vol. 53, no. 4, p. 261.
C. T.Sims:J. Metals, October, 1966, vol. 18, p. 1119.