Application of doppler broadening of annihilation radiation technique to evaluate the microhardness variations during isochronal annealing of Al and Al (Mn) alloys
Tóm tắt
Doppler broadening measurements have been carried out to study the isochronal annealing of cold-worked commercial pure Al (99.5%) and Al-1 wt.% Mn alloys. The deduced line shape and wing parameters are investigated in the range from room temperature to 823 K and correlated with the corresponding microhardness measurements. The vacancy migration and the effect of the precipitated Al6 Mn in Al (Mn) alloys could be probed as a function of annealing temperature. Three stages of microstructures can be distinguished in both Al and Al (Mn) alloys, which are recovery, partial recrystallization, and complete recrystallization. The line shape parameter-wing parameter (S-W) map indicates the same behavior in both alloys at high temperature. However, at low temperatures, Al (Mn) shows different behavior from the linear trajectory Al alloy.
Tài liệu tham khảo
Yoshiko Itoh, Hideoki Murakami, and Akira Kinoshita: Appl. Phys. Lett., 1993 vol. 63 (20), pp. 2798–99.
M. Clement, J.M.M. de Nijs, P. Balk, H. Schut, and A. Van Veen: J. Appl. Phys., 1997, vol. 81 (4), pp. 1943–55.
M. Clement, J.M.M. de Nijs, P. Balk, H. Schut, and A. Van Veen: J. Appl. Phys., 1996, vol. 79 (12), pp. 9029–36.
Positron in Solids, vol. 12, Topics in Current Physics, P. Hautojarvi, ed., Springer-Verlag, Heidelberg, 1979.
K. Peterson: Positron Solid-State Physics, North-Holland, Amsterdam, 1983, pp. 298–357.
H. Schut: Ph.D. Thesis, Technische Universiteit Delft, Delft, 1990.
G.M. Hood and R.J. Schultz: Can. J. Phys., 1982, vol. 60, pp. 1117–24.
A. Van Veen, A.C. Kruseman, H. Schut, P.E. Mijnarends, B.J. Kooi, and J.Th.M. De Hosson: Mater. Sci. Forum, 1997, vol. 255–257, pp. 67–80.
J.E. Hatch: Aluminum Properties and Physical Metallurgy, ASM, Metals Park, OH, 1984.
H.M. Fretwell, S. Usmar, A. Alam, and G. Dlubek: Mater. Sci. Forum, 1992, vol. 105–110, pp. 1013–16.
P. Cotterell and P.R. Mould: Recrystallization and Grain Growth in Metals, John Wiley & Sons, New York, NY, 1976, pp. 136–41.
C. Szeles and A. Vertes: Mater. Sci. Forum, 1992, vol. 105–110, pp. 1265–70.
C.H. Hodges: Phys. Rev. Lett., 1970, vol. 25, pp. 284–87.
P. Hautojarvi, A. Tamminen, and P. Jauho: Phys. Rev. Lett., 1970, vol. 24, pp. 459–61.
K. Mackenzie, T.L. Khoo, A.B. McDonald, and B.T.A. Mckee: Phys. Rev. Lett., 1967, vol. 19, pp. 946–48.
S. Berko and J.C. Erskine: Phys. Rev. Lett., 1967, vol. 19, pp. 307–09.