Analysis of Surface Roughness, Sound Level and Machine Current in the Turning of Hardened AISI S1 Steel
Tóm tắt
In this study, surface roughness values, sound levels and instantaneous current values were measured with calibrated devices in accordance with the experimental parameters. In this study, turning tests were carried out on AISI S1 steel material workpieces at three different depth of cuts, three different feed rates and 3 different cutting speeds without coolant. A full factorial experimental design method was used. Three different cutting speeds (135, 155, 175 m/min), feed rates (0.045, 0.090, 0.135 mm/rev) and depth of cuts (0.04, 0.08, 0.12 mm) as control factors have been selected. The effect levels on the surface roughness of the control factors with analysis of variance (ANOVA) performed using the experimental results were determined. Finally, the confirmation tests were performed and showed that the analysis is successfully implemented. As a result of analysis, the most effective cutting parameter on all the output parameters was found to be the feed rate. Its influence on the sound level was found to be 60.26%. The feed rate was followed by the cutting speed (22.87%) and the depth of cut (6.58%), respectively. The motor current values were influenced by feed rate, cutting speed and depth of cut by 52.71%, 18.73% and 23.88%, respectively.
Tài liệu tham khảo
Guerra-Zubiaga D, Mamun A A and Gonzalez-Badillo G, Int. J. Comput. Integr. Manuf. (2018). https://doi.org/10.1080/0951192X.2018.1493234.
Gutowski T, Murphy C, Allen D, Bauer D, Bras B, Piwonka T, Sheng P, Sutherland J, Thurston D and Wolff E, J. Clean. Prod. 13 (2005) 1.
Devoldere T, Dewulf W, Deprez W, Willems B and Duflou J, Improvement a for Energy Consumption in Discrete Part Production Machines, in Proceedings of the 14th CIRP Conferences on LCE, pp. 311–316 (2007).
Kahlenborn W, Kabisch S, Klein J, Richter I and Schürmann S, DIN EN 16001: Energy Management Systems in Practice—A Guide for Companies and Organisations, Germany (2010).
Karabatak M and ve Kara F, Politeknik Dergisi 19 (2016) 349 (in Turkish).
Anonymous, 60WCrV7/AISI: S1 (DIN 1.2550), Etna Celik Co. (2020). https://www.etnacelik.com.tr/1-2550/. Accessed 24/10/20.
Töenshoff H K, Arendt C and Ben Amor R, CIRP Ann. Manuf. Technol. 49 (2000) 547.
Lima J G, Avila R F, Abrao A M, Faustino M and Davim J P, J. Mater. Process. Technol. 169 (2005) 388.
Agrawal A, Goel S, Rashid W B and Price M, Appl. Soft. Comput. 30 (2015) 279.
Özel T, Karpat Y, Figueira L, and Paulo Davim J, J. Mater. Process. Technol. 189 (2007) 192.
Göloglu C and Arslan Y, J. Intell. Manuf. 20 (2009) 203.
Çiçek A, Kıvak T and Ekici E, J. Intell. Manuf. 26 (2015) 295.
Taguchi G, Chowdhury S and Wu Y, Taguchi's Quality Engineering Handbook, Wiley, New Jersey, USA (2005).
Palanikumar K, Measurement 44 (2011) 2138.
Moganapriya C, Rajasekar R, Ponappa K, Venkatesh R and Jerome S, Mater. Today Proc. 5 (2018) 8532.
Hessainia Z, Belbah A, Yallese M A, Mabrouki T and Rigal J F, Measurement 46 (2013) 1671.
Yallese M A, Chaoui K, Zeghib N, Boulanouar L and Rigal J F, J. Mater. Process. Technol. 209 (2009) 1092.
Krishna P V, Srikant R R and Rao D N, Int. J. Mach. Tools Manuf. 50 (2010) 911.
Aouici H, Yallese M A, Chaoui K, Mabrouki T and Rigal J, Measurement 45 (2012) 344.
Sahinoğlu A, Gullu A and Ciftci I, Sigma J. Eng. Nat. Sci. 37 (2019) 423.
Das D K, Sahoo A K, Das R and Routara B C, Procedia Mater. Sci. 6 (2014) 1351.
Elmunafi M H, Mohd Yusof N and Kurniawan D, Adv. Mech. Eng. 7 (2015) 1. https://doi.org/10.1177/1687814015600666.
Davim J P, J. Mater. Process. Technol. 116 (2001) 3.
Noordin M, Venkatesh V, Sharif S, Elting S and Abdullah A, J. Mater. Process. Technol. 145 (2004) 46
Yücel E and Günay M, Proc. Inst. Mech. Eng. Part C J. Mech. Eng. Sci. 227 (2013) 2280.
Mannan M, Kassim A A and Jing M, Pattern Recognit. Lett. 2121 (2000) 969.
Tekiner Z and Yeşilyurt S, Mater. Des. 25 (2004) 507
Sahinoğlu A and Gullu A, J Polytechnic (2019). https://doi.org/10.2339/politeknik.426106 (in Turkish).
Anonymous, Celik Metal Co., Products, Cold Work Tool Steels, DIN 1.2550 Steel, https://www.celikmetal.com.tr/urunlerimiz/detay/1-2550.
Stern M and Geary A L, J. Electrochem. Soc. 104 (1957) 56.
Anonymous, Hard Part Machining, Sandvik Catalogue–2019 (2020). https://www.sandvik.coromant.com/sitecollectiondocuments/downloads/global/catalogues/tr-sstr/c-2900-24.pdf. Accessed 11/11/2020.