Aerocellulose: Aerogels and Aerogel‐like Materials made from Cellulose

Macromolecular Symposia - Tập 244 Số 1 - Trang 126-135 - 2006
Josef Innerlohinger1, Hedda K. Weber1, Gregor Kraft1
1Lenzing AG, 4860 Lenzing, Austria

Tóm tắt

AbstractSummary: Cellulose aerogels have been prepared starting from cellulose‐NMMO solutions via the classical aerogel‐path. Different cellulosic materials have been tested and their influence on the properties of the product aerogels has been studied. Other parameters that have been varied include solution composition as well as the way of cellulose regeneration (solvent and temperature). More than 300 different samples were prepared and analysed. Their density is in a typical range from 0.02 g/cm3 to 0.2 g/cm3 and their internal surface area ranges from 100 m2/g to 400 m2/g. Another property investigated in detail beside density and internal surface area was the shrinkage of the cellulosic bodies during the production process.

Từ khóa


Tài liệu tham khảo

10.1021/j150331a003

10.1038/127741a0

10.1016/S0022-3093(98)00054-4

10.1023/A:1009681407649

10.1007/BF01139044

10.1016/0022-3093(95)00043-7

10.1016/S0008-6223(02)00289-0

10.1016/j.carbon.2004.10.022

10.1016/j.colsurfa.2004.03.007

10.1002/1521-4095(200105)13:9<644::AID-ADMA644>3.0.CO;2-#

Weatherwax R. C., 1971, Tappi, 54, 985

Innerlohinger J., 2006, Lenzinger Ber., 86, 137

F.Fischer E.Guilminot M.Chatenet A.Rigacci S.Berthon‐Fabry E.Chainet P.Achard “Nanostructured carbons from cellulose aerogels for PEM‐FC electrodes: elaboration and electrochemical characterization”;7th European Symposium on Electrochemical Engineering2005 Toulouse France.

10.1590/S0104-14282005000200005

10.1016/j.polymer.2006.09.004

R. N.Armstrong C. C.McCorsley J. K.Varga “Spinnable solutions of cellulose in amine oxides”;5th International Dissolving Pulps Conference1980 Atlanta USA.

10.1002/(SICI)1097-4628(19961205)62:10<1551::AID-APP7>3.0.CO;2-N

10.1016/j.ijbiomac.2004.11.008

10.1016/j.polymer.2005.08.040

10.1021/ma049300h

10.1002/1522-2640(200008)72:8<852::AID-CITE852>3.0.CO;2-S

G.Kraft in preparation.

10.1021/ja01269a023

10.1021/ja01145a126

10.1016/S0896-8446(97)00016-8

10.1016/S0001-8686(98)00051-7

10.1016/S0927-7757(01)00612-4

10.1103/PhysRevE.62.727

Thông tin
Thông tin xuất bản

Macromolecular Symposia

Tập 244 Số 1

126-135

Thông tin tác giả