A silica-silver nanocomposite obtained by sol-gel method in the presence of silver nanoparticles

Silver nanoparticles (AgNPs) were obtained by a redox reaction, using a glucose-containing cyclosiloxane as a reduction agent and stabilizer. Then the AgNPs aqueous solution was used as the reaction medium for the sol-gel process, starting from tetraethylorthosilicate (TEOS) as silica precursor. The nanocomposite material resulted (SilAg) after solvent removal, aging and calcination and was investigated by infrared spectroscopy (FT-IR), atomic force microscopy (AFM), scanning electron microscopy coupled with energy dispersive X-ray system (SEM/EDX), transmission electron microscopy (TEM), energy-dispersive X-ray fluorescence spectroscopy (EDXRF), X-ray diffraction (XRD) and dynamic vapor sorption (DVS). The results were compared to model silicas obtained without silver. A higher condensation degree in SilAg was obtained due to the basic medium used in the first step and was confirmed by a sorption capacity lower than for the model silicas. The solid surface area calculated with GAB analysis using DVS data for the water vapors is 210 m2 g−1. The nanocomposite showed good catalytic activity for hydrogen peroxide decomposition.