A promising new class of irradiation tolerant materials: Ti2ZrHfV0.5Mo0.2 high-entropy alloy

Journal of Materials Science & Technology - Tập 35 Số 3 - Trang 369-373 - 2019
Yiping Lu1, Hefei Huang2, Xuzhou Gao3, Cuilan Ren2, Jie Gao2, Huanzhi Zhang1, Shijian Zheng4, Qianqian Jin4, Yonghao Zhao3, Chenyang Lu5, Tongmin Wang1, Tingju Li1
1Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian, 116024, China
2Shanghai Institute of Applied Physics, Chinese Academy of Sciences (CAS), Shanghai 201800, China
3School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
4Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
5Department of Nuclear Engineering and Radiological Sciences, University of Michigan, Ann Arbor, MI 48109-2104, USA

Tóm tắt

Từ khóa


Tài liệu tham khảo

Zinkle, 2013, Acta Mater., 61, 735, 10.1016/j.actamat.2012.11.004

Wang, 2016, Chem. Phys. Lett., 653, 112, 10.1016/j.cplett.2016.04.074

Lv, 2018, J. Appl. Phys., 124, 10.1063/1.5066585

Allen, 2012

Boothby, 1996, J. Nucl. Mater., 230, 148, 10.1016/0022-3115(96)00169-9

Rowcliffe, 2009, J. Nucl. Mater., 392, 341, 10.1016/j.jnucmat.2009.03.023

Zinkle, 2016, Curr. Opin. Solid. State Mater., 20, 401, 10.1016/j.cossms.2016.10.004

Klueh, 2005, J. Nucl. Mater., 341, 103, 10.1016/j.jnucmat.2005.01.017

McClintock, 2009, J. Nucl. Mater., 292, 353, 10.1016/j.jnucmat.2009.03.024

Miller, 2011, J. Nucl. Mater., 418, 307, 10.1016/j.jnucmat.2011.07.031

Odette, 2008, Annu. Rev. Mater. Res., 38, 471, 10.1146/annurev.matsci.38.060407.130315

Beyerlein, 2013, Mater. Today., 16, 443, 10.1016/j.mattod.2013.10.019

Zhang, 2012, Phys. Chem. Chem. Phys., 14, 13429, 10.1039/c2cp42342a

Van Swygenhoven, 2004, Nat. Mater., 3, 399, 10.1038/nmat1136

Bringa, 2012, Nano Lett., 12, 3351, 10.1021/nl201383u

Granberg, 2016, Phys. Rev. Lett., 116, 10.1103/PhysRevLett.116.135504

Yeh, 2004, Adv. Eng. Mater., 6, 299, 10.1002/adem.200300567

Cantor, 2004, Mater. Sci. Eng. A, 375–377, 213, 10.1016/j.msea.2003.10.257

Gao, 2016

Gludovatz, 2014, Science, 345, 1153, 10.1126/science.1254581

Li, 2016, Nature, 534, 227, 10.1038/nature17981

Lu, 2016, Nat. Commun., 7, 13564, 10.1038/ncomms13564

Kiran Kumar, 2016, Acta Mater., 113, 230, 10.1016/j.actamat.2016.05.007

Zhang, 2015, Nat. Commun., 6, 8736, 10.1038/ncomms9736

Yang, 2019, J. Mater. Sci. Technol., 35

Xia, 2015, J. Iron Steel Res. Int., 22, 879, 10.1016/S1006-706X(15)30084-4

Guo, 2011, J. Appl. Phys., 109, 103505, 10.1063/1.3587228

Dong, 2014, Mater. Des., 57, 67, 10.1016/j.matdes.2013.12.048

Ziegler, 1985

Stoller, 2013, Nucl. Instrum. Methods B, 310, 75, 10.1016/j.nimb.2013.05.008

Olivier, 1992, J. Mater. Res., 7, 1564, 10.1557/JMR.1992.1564

Cao, 2013, J. Phys. Conf. Ser., 443, 10.1088/1742-6596/443/1/012017

Cao, 2014, Fusion Eng. Des., 89, 1101, 10.1016/j.fusengdes.2013.11.008

Hosemann, 2018, Scr. Mater., 143, 181, 10.1016/j.scriptamat.2017.04.027

Yvon, 2009, J. Nucl. Mater., 385, 217, 10.1016/j.jnucmat.2008.11.026

Huang, 2016, Mater. Des., 90, 359, 10.1016/j.matdes.2015.10.147

Zinkle, 2009, Mater. Today, 12, 12, 10.1016/S1369-7021(09)70294-9

Trinkaus, 2003, J. Nucl. Mater., 323, 229, 10.1016/j.jnucmat.2003.09.001

Lee, 2001, J. Nucl. Mater., 296, 183, 10.1016/S0022-3115(01)00566-9

Zhou, 2015, J. Nucl. Mater., 467, 848, 10.1016/j.jnucmat.2015.11.004

Wang, 2017, Phys. Rev. Mater., 1

Thông tin
Thông tin xuất bản

Journal of Materials Science & Technology

Tập 35 Số 3

369-373

Thông tin tác giả