A Short Review on Fracture Mechanisms of Mechanical Components Operated under Industrial Process Conditions: Fractographic Analysis and Selected Prevention Strategies
Tóm tắt
An insight of the dominant fracture mechanisms occurring in mechanical metallic components during industrial service conditions is offered through this short overview. Emphasis is given on the phenomenological aspects of fracture and their relationships with the emergent fracture mode(s) with respect to the prevailed operating parameters and loading conditions. This presentation is basically fulfilled by embracing and reviewing industrial case histories addressed from a technical expert viewpoint. The referenced case histories reflected mainly the author’s team expertise in failure analysis investigation. As a secondary perspective of the current study, selected failure investigation and prevention methodological approaches are briefly summarized and discussed, aiming to provide a holistic overview of the specific frameworks and systems in place, which could assist the organization of risk minimization and quality enhancement.
Từ khóa
Tài liệu tham khảo
Pantazopoulos, 2014, A process-based approach in failure analysis, J. Fail. Anal. Prev., 14, 551, 10.1007/s11668-014-9853-z
Wulpi, D.J. (2005). Understanding How Components Fail, ASM International. [2nd ed.].
Sachs, N.W. (2007). Practical Plant Failure Analysis, CRC Press.
González-Velázquez, J.L. (2018). Fractography and Failure Analysis, Structural Integrity 3, Springer Nature.
Broek, 1974, Some contributions of electron fractography to the theory of fracture, Int. Metall. Rev., 19, 135, 10.1179/095066074790137033
Makhlouf, A.S.H., and Aliofkhazraei, M. (2016). Progressive failures of components in chemical process industry: Case history investigation and root-cause analysis. Handbook of Materials Failure Analysis with Case Studies from Chemical, Concrete and Power Industries, Elsevier.
Pantazopoulos, 2011, Damage assessment using fractography as failure evaluation: Applications in industrial metalworking machinery, J. Fail. Anal. Prev., 11, 588, 10.1007/s11668-011-9503-7
Hosford, W.F. (2013). Solid Mechanics, Cambridge University Press.
Gurson, A.L. (1975). Plastic Flow and Fracture Behavior of Ductile Materials Incorporating Void Nucleation, Growth and Interaction. [Ph.D. Thesis, Brown University].
Tvegaard, 1984, Analysis of the cup-cone fracture in a round tensile bar, Acta Metall., 32, 157, 10.1016/0001-6160(84)90213-X
Pantazopoulos, 2016, Analysis of the degradation process of structural steel component subjected to prolonged thermal exposure, Metall. Microstruct. Anal., 5, 149, 10.1007/s13632-016-0273-1
Hull, D. (1999). Fractography: Observing, Measuring and Interpreting the Fracture Surface Topography, Cambridge University Press.
Abbasi, 2018, Investigation of the microstructure, micro-texture and mechanical properties of the HSLA steel, hot-rolled and quenched at different cooling rates, Metall. Microstruct. Anal., 7, 596, 10.1007/s13632-018-0475-9
Dieter, G.E. (1988). Mechanical Metallurgy, McGraw Hill.
Pantazopoulos, 2009, Fatigue failure of steel links operating as chain components in a heavy duty draw bench, Eng. Fail. Anal., 16, 2440, 10.1016/j.engfailanal.2009.04.005
Pantazopoulos, 2011, Analysis of failure mechanism of gripping tool steel component operated in an industrial draw bench, Eng. Fail. Anal., 18, 1595, 10.1016/j.engfailanal.2011.06.006
Pantazopoulos, 2002, Leaded brass rods C38500 for automatic machining operations, J. Mater. Eng. Perform., 11, 402, 10.1361/105994902770343926
Pantazopoulos, 2003, A review of defects and failures in brass rods and related components, Pract. Fail. Anal., 3, 14, 10.1007/BF02715925
Pantazopoulos, 2008, Failure analysis of a fractured leaded-brass (CuZn39Pb3) extruded hexagonal rod, J. Fail. Anal. Prev., 8, 218, 10.1007/s11668-007-9084-7
Pantazopoulos, 2017, Fracture analysis and embrittlement phenomena of machined brass components, Procedia Struct. Integrity, 5, 476, 10.1016/j.prostr.2017.07.146
Lynch, 2008, Failures of structures and components by metal-induced embrittlement, J. Fail. Anal. Prev., 8, 259, 10.1007/s11668-008-9124-y
Toulfatzis, 2016, Microstructure and properties of lead-free brasses using post-processing heat treatment cycles, Mater. Sci. Technol., 32, 1771, 10.1080/02670836.2016.1221493
Toulfatzis, 2018, Fracture mechanics properties and failure mechanisms of environmental-friendly brass alloys under impact, cyclic and monotonic loading conditions, Eng. Fail. Anal., 90, 497, 10.1016/j.engfailanal.2018.04.001
Totten, 2008, Fatigue crack propagation, Adv. Mater. Processes, 5, 39
Pantazopoulos, 2010, Investigation of fatigue failure of roll shafts in a tube manufacturing line, J. Fail. Anal. Prev., 10, 358, 10.1007/s11668-010-9369-0
Pantazopoulos, 2013, Failure analysis of copper tube in an industrial refrigeration unit: A case history, Int. J. Struct. Integrity, 4, 55, 10.1108/17579861311303627
Jones, D.R.H. (1993). Engineering Materials 3—Materials Failure Analysis, Pergamon Press.
Benac, 2009, Failure avoidance brief: Estimating heater tube life, J. Fail. Anal. Prev., 9, 5, 10.1007/s11668-008-9190-1
Ilman, 2014, Analysis of material degradation mechanism and life assessment of 25Cr-38Ni-Mo-Ti wrought alloy steel (HPM) for cracking tubes in an ethylene plant, Eng. Fail. Anal., 42, 100, 10.1016/j.engfailanal.2014.03.020
Quickel, 2009, Failure analysis and remaining life assessment of methanol reformer tubes, J. Fail. Anal. Prev., 9, 511, 10.1007/s11668-009-9294-2
Psyllaki, 2009, Metallurgical evaluation of creep-failed superheater tubes, Eng. Fail. Anal., 16, 1420, 10.1016/j.engfailanal.2008.09.012
Shlyannikov, 2016, Loading history effect on creep-fatigue crack growth in pipe bend, Int. J. Press. Vessels Pip., 139-140, 86, 10.1016/j.ijpvp.2016.03.007
Shlyannikov, 2018, Creep-fatigue crack growth rate assessment using ductility damage model, Int. J. Fatigue, 116, 448, 10.1016/j.ijfatigue.2018.07.003
Zerbst, 2015, Fracture mechanics as a tool in failure analysis—Prospects and limitations, Eng. Fail. Anal., 55, 376, 10.1016/j.engfailanal.2015.07.001
Murakami, 1994, Effects of defects, inclusions and inhomogeneities on fatigue strength, Int. J. Fatigue, 16, 163, 10.1016/0142-1123(94)90001-9
Pantazopoulos, 2015, Failure and fracture analysis of austenitic stainless steel marine propeller shaft, J. Fail. Anal. Prev., 15, 762, 10.1007/s11668-015-0024-7
ISO 148-1: 2009 (2009). Metallic Materials—Charpy Pendulum Impact Test. Test Method, ISO.
BS 7448-Part 1: 1991 (1991). Fracture Mechanics Tests. Determination of KIc, Critical CTOD and Critical J Values of Metallic Materials, BSI.
Toulfatzis, 2014, Fracture behavior and characterization of lead-free brass alloys for machining applications, J. Mater. Eng. Perform., 23, 3193, 10.1007/s11665-014-1096-3
Taylor, D. (2007). The Theory of Critical Distances: A New Perspective in Fracture Mechanics, Elsevier.
Cicero, S., Fuentes, J.D., Procopio, I., Madrazo, V., and González, P. (2018). Critical Distance Default Values for Structural Steels and a Simple Formulation to Estimate the Apparent Fracture Toughness in U-Notched Conditions. Metals, 8.
Li, 2001, Strain energy density failure criterion, Int. J. Solids Struct., 38, 6997, 10.1016/S0020-7683(01)00005-1
2019, Cohesive law identification of adhesive layers subject to shear load—An exact inverse solution, Int. J. Solids Struct., 158, 150, 10.1016/j.ijsolstr.2018.09.001
Pantazopoulos, 2005, Process failure modes and effects analysis (PFMEA): A structured approach for quality improvement in metal-forming industry, J. Fail. Anal. Prev., 5, 5, 10.1361/15477020522933
Toulfatzis, A., Pantazopoulos, G., David, C., Sagris, D., and Paipetis, A. (2018). Machinability of eco-friendly lead-free brass alloys: Cutting-force and surface-roughness optimization. Metals, 8.
Mariajayaprakash, 2014, Optimizing process parameters of screw conveyor (sugar mill boiler) through Failure Mode and Effect Analysis (FMEA) and Taguchi Method, J. Fail. Anal. Prev., 14, 772, 10.1007/s11668-014-9887-2
Moreno, 2015, A performance evaluation of three inference engines as expert systems for failure mode identification in shafts, Eng. Fail. Anal., 53, 24, 10.1016/j.engfailanal.2015.03.020
ISO 9001:2015 (2015). Quality Management Systems—Requirements, CEN—European Committee for Standardization.