Photoelectrochemical characteristics of TiO2 nanorod arrays grown on fluorine doped tin oxide substrates by the facile seeding layer assisted hydrothermal method
Tóm tắt
TiO2 nanorod arrays (NRAs) were prepared on fluorine doped tin oxide (FTO) substrates by a facile two-step hydrothermal method. The nanorods were selectively grown on the FTO regions which were covered with TiO2 seeding layer. It took 5 h to obtain the compact arrays with the nanorod length of ~2 μm and diameter of ~50 nm. The photoelectrochemical (PEC) properties of TiO2 NRAs are also investigated. It is demonstrated that the TiO2 NRAs indicate the good photoelectric conversion ability with an efficiency of 0.22% at a full-wavelength irradiation. A photocurrent density of 0.21 mA/cm2 is observed at 0.7 V versus the saturated calomel electrode (SCE). More evidences suggest that the charge transferring resistance is lowered at an irradiation, while the flat-band potential (V
fb) is shifted towards the positive side.
Tài liệu tham khảo
M. M. Momeni and Y. Ghaye, Journal of Electroanalytical Chemistry 751, 43 (2015).
X. C. Ni, L. X. Sang, H. J. Zhang, A. Kiliyanamkandy, S. Amoruso, X. Wang, R. Fittipaldi, T. Li, M. L. Hu and L. J. Xu, Optoelectronics Letters 10, 43 (2014).
B. O’Regan and M. Grätzel, Nature 353, 737 (1991).
J. R. Jenning, A. Ghicov, L. M. Peter, P. Schmuki and A. B. Walker, Journal of American Chemical Society 130, 13364 (2008).
B. L. Xu, C. X. Liu, H. Y. Sun and Y. R. Zhong, Optoelectronics Letters 10, 84 (2014).
S. A. Berhe, S. Nag, Z. Molinets and W. J. Youngblood, ACS Applied Materials & Interfaces 54, 573 (2013).
D. D. Qin, Y. P. Bi, X. J. Feng, W. Wang, G. D. Barber, T. Wang, Y. M. Song, X. Q. Lu and T. E. Mallouk, Chemistry of Materials 27, 4180 (2015).
M. Lv, D. Zheng, M. Ye, J. Xiao, W. Guo, Y. Lai, L. Sun, C. Lin and J. Zuo,, Energy & Environmental Science 6, 1615 (2013).
A. Yella, L. P. Heiniger, P. Gao, M. K. Nazeeruddin and M. Grätzel, Nano Letters 14, 2591 (2014).
A. Wolcott, W. A. Smith, T. R. Kuykendall, Y. Zhao and J. Z. Zhang, Small 5, 104 (2009).
X. Gu, S. Zhang, Y. Qiang, Y. Zhao and L. Zhu, Journal of Electronic Materials 43, 2709 (2014).
Z. Li, W. Luo, M. Zhang, J. Feng and Z. Zou, Energy & Environmental Science 6, 347 (2013).
M. Sui, C. Han, X. Gu, Y. Wang, L. Tang and H. Tang, Optoelectronics Letters 11, 405 (2015).
T. J. Jacobsson and T. Edvinsson, Journal of Physical Chemistry C 116, 15692 (2012).
H. P. Maruska and A. K. Ghosh, Solar Energy 20, 443 (1978).
E. Burstein,, Phys. Rev. B 93, 632 (1954).