Orthorhombic–tetragonal phase coexistence and piezoelectric behavior in (1−x)(Ba,Ca)(Ti,Sn)O3–x(Ba,Ca)(Ti,Zr)O3 lead-free ceramics

Materials Research Bulletin - Tập 48 - Trang 4411-4414 - 2013
Jiagang Wu1, Arzigul Habibul1, Xiaojing Cheng1, Xiaopeng Wang1, Binyu Zhang1
1Department of Materials Science, Sichuan University, 610064, PR China

Tài liệu tham khảo

Rodel, 2009, J. Am. Ceram. Soc., 92, 1153, 10.1111/j.1551-2916.2009.03061.x Zhang, 2007, J. Electroceram., 19, 251, 10.1007/s10832-007-9056-z Zhou, 2012, J. Mater. Sci., 47, 1767, 10.1007/s10853-011-5957-y Saito, 2004, Nature, 432, 84, 10.1038/nature03028 Wu, 2007, Appl. Phys. Lett., 91, 252907, 10.1063/1.2827573 Guo, 2004, Appl. Phys. Lett., 85, 4121, 10.1063/1.1813636 Li, 2006, J. Am. Ceram. Soc., 89, 706, 10.1111/j.1551-2916.2005.00743.x Zuo, 2010, J. Am. Ceram. Soc., 93, 2783, 10.1111/j.1551-2916.2010.03804.x Lin, 2006, Appl. Phys. Lett., 88, 062901, 10.1063/1.2171799 Wang, 2004, Appl. Phys. Lett., 85, 91, 10.1063/1.1767592 Liu, 2009, Phys. Rev. Lett., 103, 257602, 10.1103/PhysRevLett.103.257602 Cross, 2004, Nature, 432, 24, 10.1038/nature03142 Xue, 2011, Appl. Phys. Lett., 99, 122901, 10.1063/1.3640214 Li, 2012, Ceram. Int., 38, 4353, 10.1016/j.ceramint.2011.12.066 Li, 2010, J. Am. Ceram. Soc., 93, 2942, 10.1111/j.1551-2916.2010.03907.x Zhou, 2012, Appl. Phys. Lett., 100, 222910, 10.1063/1.4724216 Xue, 2012, Europhys. Lett., 100, 17010, 10.1209/0295-5075/100/17010 Lin, 2013, J. Mater. Sci. Mater. Electron., 24, 734, 10.1007/s10854-012-0802-x Cui, 2012, Ceram. Int., 38, 4761, 10.1016/j.ceramint.2012.02.063 Takahashi, 2006, Jpn. J. Appl. Phys., 45, L30, 10.1143/JJAP.45.L30 Wu, 2012, Mater. Res. Bull., 47, 1281, 10.1016/j.materresbull.2012.01.032 Wu, 2013, J. Alloys Compd., 576, 299, 10.1016/j.jallcom.2013.04.099 Hao, 2012, J. Am. Ceram. Soc., 95, 1998, 10.1111/j.1551-2916.2012.05146.x