Microstructure and technological plasticity of cast intermetallic alloys on the basis of γ-TiAl
Tóm tắt
This work is devoted to the estimation of the technological plasticity of binary and alloyed γ titanium aluminides by conducting compression tests at T = 1000°C. The technological plasticity was shown to grow with decreasing size of grains and grain colonies and with increasing amount of β-stabilizing elements in the alloys. The best technological properties are characteristic of the alloys that solidify completely through the β phase, containing β-stabilizing additions of niobium and molybdenum and microadditions of boron. These alloys are characterized by a small size of crystallites in the cast state; the use of special heat treatments makes it possible to substantially decrease the fraction of the lamellar component and to increase the content of the β(B2) phase in them. For the most technological alloy, tensile tests in the cast state have been carried out. In the temperature range of T = 900–1100°C, superplastic elongations have been achieved.
Tài liệu tham khảo
L. E. Popov, Mechanical. Properties of Ordered Solid Solutions, Ed. by L. E. Popov and E. V. Kozlov (Metallurgiya, Moscow, 1970) [in Russian].
S. L. Semiatin, J. C. Chesnutt, C. M. Austin, et al., “Processing of Intermetallic Alloys,” in Proc. 2nd Int. Symp. on Structural Intermetallics, Ed. by M. V. Nathal, R. Darolia, C. T. Liu, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 1997), pp. 263–276.
P. L. Martin, D. A. Hardwick, D. R. Clemens, et al., “Scale-Up of Ingot Metallurgy Wrought Gamma-TiAl,” in Proc. 2nd Int. Symp. on Structural Intermetallics, Ed. by M. V. Nathal, R. Darolia, C. T. Liu, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 1997), pp. 387–394.
W. J. Porter, Y.-W. Kim, K. Li, et al., “Primary Melting Issues Related to Gamma Titanium Aluminides,” in Proc. 3d Int. Symp. on Structural Intermetallics, Ed. by K. J. Hemker, D. M. Dimiduk, H. Clemens, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 2001), pp. 200–206.
R. M. Imaev, V. M. Imaev, T. G. Khismatullin, et al., “New Approaches to Designing Alloys Based on γ-TiAl + α2-Ti3Al Phases,” Fiz. Met. Metalloved. 102(1), 1–9 (2006) [Phys. Met. Metallogr. 102 (1), 105–113 (2006)].
R. Imayev, V. Imayev, M. Oehring, and F. Appel, “Alloy Design Concepts for Refined Cast and Wrought Gamma Titanium Aluminide Based Alloys,” Intermetallics 15(4), 451–460 (2007)
H. Clemens, W. Wallgram, S. Kremmer, et al., “Design of Novel β-Solidifying TiAl Alloys with Adjustable β/B2-Phase Fraction and Excellent Hot-Workability,” Adv. Eng. Mater. 10, 707–713 (2008).
V. M. Imaev, R. M. Imaev, and T. G. Khismatullin, “Mechanical Properties of the Cast Intermetallic Alloy Ti-43Al-7(Nb,Mo)-0.2B (at %) after Heat Treatment,” Fiz. Met. Metalloved. 105(5), 516–522 (2008) [Phys. Met. Metallogr. 105 (5),484–490 (2008)].
V. M. Imaev, R. M. Imaev, A. V. Kuznetsov, et al., “New Approaches to the Thermomechanical Treatment of Cast Intermetallic Alloys Based on Aluminides (γ-TiAl + α2-Ti3Al),” Fiz. Met. Metalloved. 100(2), 51–62 (2005) [Phys. Met. Metallogr. 100 (2), 142–152 (2005)].
R. M. Imayev, V. M. Imayev, M. Oehring, and F. Appel, “Microstructural Evolution during Hot Working of Ti Aluminide Alloys: Influence of Phase Constitution and Initial Casting Texture,” Metall. Trans. A, 36, 859–867 (2005).
S. L. Semiatin and V. Seetharaman, “A Criterion for Intergranular Failure during Hot Working of a Near-Gamma Titanium Aluminide Alloy,” Scr. Metall. Mater. 36(3), 291–297 (1997).
S. L. Semiatin, V. Seetharaman, and I. Weiss, “Hot Workability of Titanium and Titanium Aluminide Alloys-Overview,” Mater. Sci. Eng., A 243, 1–24 (1998).
Y.-W. Kim and D. M. Dimiduk, “Designing Gamma TiAl Alloys: Fundamentals, Strategy and Production,” in Proc. 2nd Int. Symp. on Structural Intermetallics, Ed. by M. V. Nathal, R. Darolia, C. T. Liu, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 1997), pp. 531–543.
Y.-W. Kim and D. M. Dimiduk, “Effect of Boron Addition on Grain Refinement and Lamellar Formation in Wrought-Processed Gamma TiAl Alloys,” in Proc. 3d Int. Symp. on Structural Intermetallics, Ed. by K. J. Hemker, D. M. Dimiduk, H. Clemens, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 2001), pp. 625–632.
F. Appel, M. Oehring, J. D. H. Paul, and U. Lorenz, “Design, Properties and Processing of Novel TiAl Alloys,” in Proc. 3d Int. Symp. onStructural Intermetallics, Ed. by K. J. Hemker, D. M. Dimiduk, H. Clemens, et al. (The Minerals, Metals and Materials Society, Warrendale, PA, 2001), pp. 63–72.
Chr. Herzig, T. Przeorski, M. Friesel, et al., “Tracer Solute Diffusion of Nb, Zr, Cr, Fe, and Ni in γ-TiAl: Effect of Preferential Site Occupation,” Intermetallics 9(6), 461–472 (2001).
F. Appel, M. Oehring, and R. Wagner, “Novel Design Concepts for Gamma-Base Titanium Aluminide Alloys,” Intermetallics 8(9–11), 1283–1312 (2000).