Study of transformation plasticity in tetragonal zirconia polycrystals by moiré interferometry
Tóm tắt
Transformation plasticity in ceria-stabilized tetragonal zirconia polycrystals due to the stress-induced tetragonal-to-monoclinic martensitic transformation under tension and bending is studied by moiré interferometry. The whole fringe patterns includingu fields andv fields are acquired. According to these patterns, the distributions of transformation plasticity in transformation zones are obtained, and the phenomenon of plastic flow localization for transformation is revealed. The above work provides a significant experimental foundation for establishing transformation constitutive relations