Creep-resistant porous structures based on stereo-complex forming triblock copolymers of 1,3-trimethylene carbonate and lactides
Tóm tắt
Stereo-complexes (poly(ST–TMC–ST)) of enantiomeric triblock copolymers based on 1,3-trimethylene carbonate (TMC) and L- or D-lactide (poly(LLA–TMC–LLA) and poly(DLA–TMC–DLA)) were prepared. Films of poly(ST–TMC–ST) could be prepared by solvent casting mixtures of equal amounts of poly(LLA–TMC–LLA) and poly(DLA–TMC–DLA) solutions and by compression moulding co-precipitates. Although compression moulding was performed at 191 °C, thermal degradation was not apparent and materials with good tensile properties could be obtained. For compression-moulded poly(ST–TMC–ST) specimens containing approximately 16 mol % lactide, the values for E-modulus, yield stress and elongation at break were respectively 17, 1.7 MPa and 90%. Also a very low long-term creep rate of 2.2×10−7 s−1 was determined when specimens were loaded to 20% of the yield stress. When compared with compression-moulded poly(TMC), poly(ST–TMC–ST) specimens deform at a rate that is one to two orders of magnitude lower. Furthermore, poly(ST–TMC–ST) specimens showed complete dimensional recovery within 24 h after loading to 20% and 40% of the yield stress for 40 and 5.5 h, respectively. Highly porous poly(TMC) and poly(ST–TMC–ST) structures with interconnected pores were prepared by a method combining co-precipitation, compression moulding and salt leaching. After prolonged compressive deformation, solid and porous poly(ST–TMC–ST) discs showed significantly better recovery behaviour than poly(TMC) discs.
Tài liệu tham khảo
citation_journal_title=J. Biomech.; citation_author=T. D. Brown; citation_volume=33; citation_publication_date=2000; citation_pages=3; citation_id=CR1
citation_journal_title=Ann. Biomed. Eng.; citation_author=J. P. Stegemann, R. M. Nerem; citation_volume=31; citation_publication_date=2003; citation_pages=391; citation_id=CR2
citation_journal_title=Ann. Biomed. Eng.; citation_author=H. Y. Shin, M. E. Gerritsen, R. Bizios; citation_volume=30; citation_publication_date=2002; citation_pages=279; citation_id=CR3
citation_journal_title=Nat. Biotechnol.; citation_author=B.-S. Kim, J. Nikolovski, J. Bonadio, D. J. Mooney; citation_volume=17; citation_publication_date=1999; citation_pages=979; citation_id=CR4
citation_journal_title=J. Biomed. Eng.-Trans. ASME; citation_author=B.-S. Kim, D. J. Mooney; citation_volume=122; citation_publication_date=2000; citation_pages=210; citation_id=CR5
citation_journal_title=J. Biomed. Eng.-Trans. ASME; citation_author=R. L. Mauck, M. A. Soltz, C. C. B. Wang, D. D. Wong, P. G. Chao, W. B. Valhmu, C. T. Hung, G. A. Ateshian; citation_volume=122; citation_publication_date=2000; citation_pages=252; citation_id=CR6
citation_journal_title=J. Biomed. Mater. Res.; citation_author=A. P. Pégo, M. J. A. Van Luyn, L. A. Brouwer, P. B. Van Wachem, A. A. Poot, D. W. Grijpma, J. Feijen; citation_volume=67A; citation_publication_date=2003; citation_pages=1044; citation_id=CR7
citation_journal_title=Tissue Eng.; citation_author=A. P. Pégo, B. Siebum, M. J. A. Van Luyn, X. J. Gallego, Y Van Seijen, A. A. Poot, D. W. Grijpma, J. Feijen; citation_volume=9; citation_publication_date=2003; citation_pages=981; citation_id=CR8
citation_journal_title=J. Biomed. Mater. Res.; citation_author=A. P. Pégo, C. L. A. M. Vleggeert-Lankamp, M. Deenen, E. A. J. F. Lakke, D. W. Grijpma, A. A. Poot, E. Marani, J. Feijen; citation_volume=67A; citation_publication_date=2003; citation_pages=876; citation_id=CR9
citation_journal_title=Macromolecules; citation_author=Y. Ikada, K. Jamshidi, H. Tsuji, S.-H. Hyon; citation_volume=20; citation_publication_date=1987; citation_pages=904; citation_id=CR10
citation_journal_title=Macromolecules; citation_author=H. Tsuji, S.-H. Hyon, Y. Ikada; citation_volume=24; citation_publication_date=1991; citation_pages=5651; citation_id=CR11
Z. Zhang, D. W. Grijpma and J. Feijen, Macromol. Chem. Phys. (2004) accepted.
citation_journal_title=Macromol. Rapid Commun.; citation_author=Q. P. Hou, D. W. Grijpma, J. Feijen; citation_volume=23; citation_publication_date=2002; citation_pages=247; citation_id=CR13
citation_journal_title=J. Biomat. Sci. Polym. Ed.; citation_author=A. P. Pégo, A. A. Poot, D. W. Grijpma, J. Feijen; citation_volume=12; citation_publication_date=2001; citation_pages=35; citation_id=CR14
citation_journal_title=Polymer; citation_author=A. P. Pégo, D. W. Grijpma, J. Feijen; citation_volume=44; citation_publication_date=2003; citation_pages=6495; citation_id=CR15
citation_journal_title=Colloid Polym. Sci.; citation_author=J. P. Penning, H. E. Pras, A. J. Pennings; citation_volume=272; citation_publication_date=1994; citation_pages=664; citation_id=CR16