Phase transition behavior and electrical properties of lead-free (1-x)KNLNS-xBNKZ piezoelectric ceramics
Tóm tắt
Lead-free (1-x)(K0,48Na0,48Li0,04)(Nb0,95Sb0,05)O3-xBi0.5(Na0.82K0.18)0.5ZrO3 (KNLNS-xBNKZ) piezoelectric ceramics (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) were successfully prepared by the two-step sintering method. The effects of different BNKZ contents on the crystal structure, ferroelectric phase transition, and electrical properties of the as-prepared ceramics were systematically researched. The ceramics with a perovskite structure possessed an orthorhombic phase (space group = Amm2) at x = 0, a mixed orthorhombic-tetragonal phase (Amm2 + P4/mbm) at x = 0.02, a mixed rhombohedral-tetragonal (R-T) phase (R3m + P4/mbm) at x = 0.04–0.06, and a rhombohedral phase (R3m) at x>0.06. At x = 0.04 (rhombohedral and tetragonal (R-T) phases coexisted), the ceramics manifested the best electrical properties with d33 = 224 pC/N, kp = 0.44, kt = 0.47, TC = 218oC, and remanent polarization (Pr) = 11.5µC/cm2. The improvement of the electrical properties of KNLNS-BNKZ ceramics was achieved by controlling their phase compositions and microstructures.
Tài liệu tham khảo
P.D. Gio, V.D. Dan, J. Alloys Compd. 449(1–2), 24–27 (2008)
N.D.T. Luan, L.D. Vuong, T. Van Chuong, N. Truong, Tho, Adv. Mater. Sci. Eng. 2014, 821404 (2014)
L.D. Vuong, P.D. Gio, N.D.V. Quang, T.D. Hieu, T.P. Nam, J. Electron. Mater. 47(10), 5944–5951 (2018)
L.D. Vuong, V.T. Tung, P.D. Gio, The investigation on the fabrication and characterization of the multicomponent ceramics based on PZT and the relaxor. (PZN-PMnN Ferroelectric Materials/ Ceramic Materials, IntechOpen, 2020)
L.D. Vuong, P.D. Gio, J. Mod. Phys. 05(14), 1258–1263 (2014)
N.D.T. Luan, L.D. Vuong, B.C. Chanh, Int. J. Mater. Chem. 3(3), 51–58 (2013)
P.D. Gio, H.Q. Viet, L.D. Vuong, Int. J. Mater. Res. 109(11), 1071–1076 (2018)
L.D. Vuong, N.T. Tho, Int. J. Mater. Res. 108(3), 222–227 (2017)
D.V. Le, A.Q. Dao, J. Electroceram. 44(1), 68–77 (2020)
X. Cheng, J. Wu, X. Wang, B. Zhang, J. Zhu, D. Xiao, X. Wang, X. Lou, Appl. Phys. Lett. 103(5), 052906 (2013)
D.A. Tuan, L.D. Vuong, V.T. Tung, N.N. Tuan, N.T. Duong, J. Ceram. Process. Res. 19(1), 32–36 (2018)
L-FP Ceramics, J. Mater. Sci. Chem. Eng. 3, 13–20 (2015)
P.D. Gio, N.T.K. Lien, Indian J. Sci. Res. Technol. 3(5), 48–53 (2015)
Q. Gou, D.-Q. Xiao, B. Wu, M. Xiao, S.-S. Feng, D.-D.M. Zhao, J.-G. Wu, J.-G. Zhu, RSC Adv. 5(39), 30660–30666 (2015)
Y. Cheng, J. Xing, C. Wu, T. Wang, L. Xie, Y. Liu, X. Xu, K. Wang, D. Xiao, J. Zhu, J. Alloys Compd. 815, 152252 (2020)
Y. Zhang, S. Wang, C. Chen, N. Zhang, A. Wang, Y. Zhu, F. Cai, Ceram. Int. 44(7), 8380–8386 (2018)
P.D. Gio, L.D. Vuong, L.T.U. Tu, Mater. Sci. Mater. Electron. 32(10), 13738–13747 (2021)
M. Matsubara, K. Kikuta, S. Hirano, J. Appl. Phys. 97(11), 114105 (2005)
J. Tangsritrakul, D.A. Hall, Adv. Appl. Ceram. 117(1), 42–48 (2018)
X. Wang, J. Wu, D. Xiao, J. Zhu, X. Cheng, T. Zheng, B. Zhang, X. Lou, C.S. Wang, J. Am. Chem. Soc. 136(7), 2905–2910 (2014)
D. Wang, F. Hussain, A. Khesro, A. Feteira, Y. Tian, Q. Zhao, I.M. Reaney, J. Am. Ceram. Soc. 100(2), 627–637 (2017)
T. Zheng, J. Wu, J. Mater. Chem. A 3(13), 6772–6780 (2015)
B. Liu, Y. Zhang, P. Li, B. Shen, J. Zhai, Ceram. Int. 42(12), 13824–13829 (2016)
X. Lv, J. Wu, D. Xiao, H. Tao, Y. Yuan, J. Zhu, X. Wang, X. Lou, Dalton Trans. 44(10), 4440–4448 (2015)
J. Ma, J. Wu, B. Wu, RSC Adv. 8(52), 29871–29878 (2018)
J. Xing, Z. Tan, L. Jiang, Q. Chen, J. Wu, W. Zhang, D. Xiao, J. Zhu, J. Appl. Phys. 119(3), 034101 (2016)
L.D. Vuong, P.D. Gio, J. Alloys Compd. 817, 152790 (2020)
S. Dwivedi, T. Pareek, S. Kumar, RSC Adv. 8(43), 24286–24296 (2018)