Differential scanning calorimetry an essential tool to characterize LiMn2O4 spinel
Tóm tắt
A series of LiMn2O4 samples with nominal Li/Mn molar ratio=1/2 has been synthesized at 700 and 750°C by the ceramic procedure from Mn2O3 and several lithium sources. Lattice parameters determined from X-ray diffraction patterns are within a narrow range, from a
c=8.238(1) Å to a
c=8.245(1) Å, Da
c/a
c<0.1%. The study by differential scanning calorimetry (DSC) shows that the temperatures of the cubic (Fd3m)↔orthorhombic (Fddd) phase transition are spread off in a wide range, from -30 to -2°C for the exothermic C→O phase transition, and from -21 to +13°C for the endothermic O→C transformation. Relationships between the lattice parameter values, the temperature of the phase transformation, and the stoichiometry of the LiMn2O4 samples are pointed out. The DSC technique, which reveals more sensitive than X-ray diffraction to very small variations of composition, is put forward as an essential technique to characterize LiMn2O4 samples.
Tài liệu tham khảo
Y. Nishi, in 'Lithium Ion Batteries: Fundamentals and Performance', M. Wakihara, O. Yamamoto Eds Wiley-VCH, Tokyo, Chap. 8 (1998).
J. R. Owen, Chem. Soc. Rev., 26 (1997) 259.
B. Scrosati, Electrochim. Acta, 45 (2000) 2461.
M. Winter, J. O. Beneshad, M. E. Sparth and P. Novák, Adv. Mater., 10 (1998) 725.
M. M. Tackeray, Prog. Solid State Chem., 25 (1997) 1.
J. M. Paulsen and J. R. Dahn, Chem. Mater., 11 (1999) 3065.
X. Sun, H. S. Lee, X. Q. Yang and J. McBreen, Electrochem. Solid State Lett., 4 (2001) A184.
V. Manev, B. Banov, A. Momchilov and A. Nassalevska, J. Power Sources, 57 (1995) 99.
M. M. Thackeray and M. H. Rossouw, J. Solid State Chem., 113 (1994) 441.
Y. Gao and J. R. Dahn, J. Electrochem. Soc., 143 (1996) 100.
S. R. S. Prabaharan, M. S. Michael, T. P. Kumar, A. Mani, K. Athinarayanaswamy and R. Gangadharan, J. Mater. Chem., 5 (1995) 1035.
W. Liu, G.C. Farrington, F. Chaput and B. Dunn, J. Electrochem. Soc., 143 (1996) 879.
V. Massaroti, D. Capsoni, M. Bini, G. Chiodelli, C. B. Azzoni, M. C. Mozzati and A. Paleari, J. Solid State Chem., 147 (1999) 509.
W. Yang, X. Huang and L. Chen, J. Power Sources, 81-82 (1999) 647.
N. V. Kosova, N. F. Uvanov, E. T. Devyatkina, E. G. Awakumov and S. Y. Solomentsev, Russ. J. Appl. Chem., 73 (2000) 436.
W. Yang, G. Zhang, J. Xie, L. Yang and Q. Liu, J. Power Sources, 81-82 (1999) 412.
A. Yamada, K. Miura, K. Hinokuma and M. Tanaka, J. Electrochem. Soc., 142 (1995) 2149.
Y. K. Sun, K. H. Lee, S. I. Moon and I. H. Oh, Solid State Ionics, 112 (1998) 237.
T. Nakamura and A. Kajiyama, Solid State Ionics, 124 (1999) 45.
D. S. Ahn and M. Y. Song, J. Electrochem. Soc., 147 (2000) 874.
S. Xia, T. Sakai, T. Fujideda, X. Q. Yang, X. Sun, Z. F. Ma, J. Mcbreen and M. Yoshio, J. Electrochem. Soc., 148 (2001) A723.
A. Yamada and M. Tanaka, Mat. Res. Bull., 30 (1995) 715.
K. Oikawa, T. Kamiyama, F. Izumi, B. C. Chakoumakos, H. Ikuta, M. Wakihara, J. Li and Y. Matsui, Solid State Ionics, 109 (1998) 35.
J. Rodríguez-Carvajal, G. Rousse, C. Masquelier and M. Hervieu, Phys. Rev. Lett., 81 (1998) 4660.
G. Rousse, C. Masquelier, J. Rodríguez-Carvajal and M. Hervieu, Electrochem. Solid-State Lett., 2 (1999) 6.
A. Yamada, J. Solid State Chem., 122 (1996) 160.
G. G. Amatucci, C. N. Schmutz, A. Blyr, C. Sigala, A. S. Gozdz, D. Larcher and J. M. Tarascon, J. Power Sources, 69 (1997) 11.
J. M. Amarilla, Bol. Soc. Esp. Cerám. Vidrio., 34 (1995) 463.
J. Laugier and A. Filhol (CelRef), ILL, Grenoble, France, unpublised, PC version, 1991.
R. J. Gummow, A. de Kock and M. M. Tackeray, Solid State Ionics, 69 (1994) 59.
Y. Xia and M. Yoshio, J. Power Sources, 57 (1995) 125.
C. Masquelier, M. Tabuchi, K. Ado, R. Kanno, Y. Kobayashi, Y. Maki, O. Nakamura and J. B. Goodenough, J. Solid State Chem., 123 (1996) 255.
Y. M. Hon, H. Y. Chung, K. Z. Fung and M. H. Hon, J. Solid State Chem., 160 (2001) 368.
X. Q. Yang, X. Sun, M. Balasubramanian, J. McBreen, Y. Xia, T. Sakai and M. Yoshio, Electrochem. Solid State Lett., 4 (2001) A117.
R. D. Shannon, Acta Crystallogr., A32 (1976) 751.
R. C. Mackenzie, in 'Differential Thermal Analysis', Vol. 1, Academic Press, London 1970, p. 108.
W. W. Wendlandt, in 'Thermal Methods of Analysis', Wiley 1974, p. 173.
E. J. W. Verwey and P. W. Haaymann, Physica, 8 (1941) 979.
E. J. W. Verwey, P. W. Haayman and F. C. Romeijn, J. Phys. Chem., 15 (1947) 181.
V. A. M. Brabers, F. Walz and H. Kronmüller, Phys. Rev. B, 58 (1998) 163.