Calciothermic reduction of titanium oxide in molten CaCl2
Tóm tắt
Titanium oxides were reduced to metallic titanium using the liquid calcium floating on the molten CaCl2. A part of Ca dissolved into CaCl2 and reacted with TiO2 settled below CaCl2. The by-product CaO also dissolved by about 20 mol pct into CaCl2, which was effective in reducing the oxygen concentration in the obtained Ti particles. The compositional region in the Ca-CaCl2-CaO system was examined for the less oxygen contamination in Ti and the better handling in leaching. A large amount of the residual calcium oxidized the titanium powder in leaching. The metallic Ti powder less than 1000 mass ppm oxygen could be obtained only for 3.6 ks using 5 to 7 mol pct Ca-CaCl2 at 1173 K. The powder was slightly sintered like sponge, and contained approximately 1500 ppm Ca. The anatase phae, the intermediate product in the refining process of TiO2, could be also supplied as raw material as well as rutile.
Tài liệu tham khảo
W. Kroll: Trans. Electrochem. Soc., 1940, vol. 78, pp. 35–47.
K. Ono and R.O. Suzuki: Mater. Jpn., 2002, vol. 41 (1), pp. 28–31.
O. Kubaschewski and W.A. Dench: J. Inst. Met., 1953, vol. 82, pp. 87–91.
K. Ono, T.H. Okabe, M. Ogawa, and R.O. Suzuki: Tetsu-to-Hagané, 1990, vol. 76 (4), pp. 568–75.
W. Kroll and Z. Anorg: Allgem. Chem., 1937, vol. 234, pp. 42–50.
S. Miyazaki, T. Oishi, and K. Ono: Titanium, Science and Technology, Proc. 5th. Int. Conf. on Titanium, Munich, Germany, Sept. 10–14, 1984, G. Luetjering, U. Zwicker, and W. Bunk, eds., Deutsche Geselschaft fuer Metallk., Oberursel, Germany, 1985, pp. 2657–63.
K. Ono and S. Miyazaki: J. Jpn. Inst. Metall., 1985, vol. 49 (10), pp. 871–75.
R.O. Suzuki, M. Ogawa, T. Oishi, and K. Ono: Proc. 6th World Conf. on Titanium 1988, Cannes, France Soc. Franc. Metall., Paris, 1989, vol. II, pp. 701–06.
T.H. Okabe, R.O. Suzuki, T. Oishi, and K. Ono: Mater. Trans. JIM, 1991, vol. 32 (5), pp. 485–88.
H. Niiyama, Y. Tajima, F. Tsukihashi, and N. Sano: J. Less-Common Met., 1991, vol. 169, pp. 209–16.
I. Obinata, Y. Takeuchi, and S. Saikawa: Trans. ASM, 1960, vol. 52, pp. 1072–83.
P.P. Alexander: U.S. Patent 2,038,402, 1936; U.S. Patent 2,043, 363, 1936; and U.S. Patent 2,082,134, 1937.
B. Neumann, C. Kroeger, and H. Juettner: Z. Elektrochem., 1935, vol. 41 (10), pp. 725–36.
D.A. Wenz, I. Johnson, and R.D. Wolson: J. Chem. Eng. Data, 1969, vol. 14 (2), pp. 250–52.
G.S. Perry and L.G. MacDonald: J. Nucl. Mater., 1985, vol. 130, pp. 234–41.
T.H. Okabe, R.O. Suzuki, T. Oishi, and K. Ono: Tetsu-to-Hagané, 1991, vol. 77 (1), pp. 93–99.
T.H. Okabe, T. Oishi, and K. Ono: J. Alloys Compounds, 1992, vol. 184, pp. 43–56.
T.H. Okabe, M. Nakamura, T. Ueki, T. Oishi, and K. Ono: Bull. Jpn. Inst. Met., 1992, vol. 31 (4), pp. 315–17.
S. Liu, R.O. Suzuki, and K. Ono: J. Alloys Compounds, 1998, vol. 266, pp. 247–54.
R.O. Suzuki, M. Aizawa, and K. Ono: J. Alloys Compounds, 1999, vol. 288, pp. 173–82.
T.H. Okabe, T.N. Deura, T. Oishi, K. Ono, and D.R. Sadoway: Metall. Mater. Trans. B, 1996, vol. 27B, pp. 841–47.
T.H. Okabe, K. Hirota, Y. Waseda, and K.T. Jacob: Shigen-to-Sozai, 1998, vol. 114 (11), pp. 813–18.
T.H. Okabe, K. Hirota, E. Kasai, F. Saito, Y. Waseda, and K.T. Jacob: J. Alloys Compounds, 1998, vol. 279, pp. 184–91.
R.O. Suzuki, A. Saguchi, K. Asabe, T. Takahashi, T. Yagura, and K. Ono: Mater. Trans., 2001, vol. 42 (12), pp. 2492–98.
K. Ono: Titanium Jpn., 2000, vol. 48 (1), pp. 13–15.
K. Ono and R.O. Suzuki: JOM Mem. J. Min. Met. Mater. Soc., 2002, vol. 54 (2), pp. 59–61.
K. Ono and R.O. Suzuki: Titanium Jpn., 2002, vol. 50 (2), pp. 105–8.
M.S. Coops, J.B. Knighton, and L.J. Mullins: ACS Symposium Series No. 216, Pulutonium Chemistry, W.T. Carnall and G.R. Choppin, eds., 1983, pp. 381–408.
A. Roine: HSC Chemistry for Windows, ver. 4.1, Outokump Research Oy, Pori, Finland.
V. Dosaj, C. Aksaranan, and D.R. Morris: J. Chem. Soc. Faraday Trans., 1975, vol. 71, pp. 1083–98.
H. Fischbach: Steel Res., 1985, vol. 56 (7), pp. 365–68.
L.-I. Staffansson and D. Sichen: Scand. J. Metall., 1992, vol. 21, pp. 165–71.
K.M. Axler and G.L. DePoorter: Mater. Sci. Forum, 1991, vols. 73–75, pp. 19–24.
Metals Databook, Japan Institue of Metals, 2nd ed., Maruzen, Tokyo, 1984, pp. 15 and 68.
T.N. Deura, M. Wakino, T. Matsunaga, R.O. Suzuki, and K. Ono: Metall. Mater. Trans. B, 1998, vol. 29B, pp. 1167–74.
R.O. Suzuki, T.N. Harada, T. Matsunaga, T.N. Deura, and K. Ono: Metall. Mater. Trans. B, 1999, vol. 30B, pp. 403–10.
Y. Ochifuji, F. Tsukihashi, and N. Sano: Metall. Mater. Trans. B, 1995, vol. 26B, pp. 789–94.
Y. Tago, Y. Endo, K. Morita, F. Tsukihashi, and N. Sano: Iron Steel Inst. Jpn. Int., 1995, vol. 36 (2), pp. 127–31.