Thermal Behavior of Hybrid Composite, Giomer, Ormocer and Silorane: A Comparative Study Using Two Light Curing Intensities
Tóm tắt
Purpose of the study was to evaluate the effect of type of composite resin (CR) and the intensity of curing device on thermal behavior. A microhybrid composite (C), a giomer (G), an ormocer (O) and silorane (S) were chosen. Specimens were polymerized with a higher (H) and a lower (L) energy LED curing device. Coefficient of thermal expansion (CTE) measurements were performed with a dilatometer at temperature range 20-60ºC with temperature raise 2ºC/min. CTE values in lower temperatures (21ºC-37ºC) (CTEa) were compared to CTE values in higher temperatures (37ºC-55ºC) (CTEb). CTEa for all resin composites ranged from 5.43 - 38.67 (x 10-6/ºC) and CTEb from 22.20 - 48.87 (x 10-6/ºC), thus depending on CR type, curing intensity and temperature range. Type of CR and light intensity of curing device have an effect on thermal behavior. The higher the temperature, the higher the CTE for all materials. It is advisable to polymerize C with lower intensity curing unit and S and O with higher intensity. G exhibits the highest CTE values with both curing devices, while O exhibits intermediate results with both light intensities in all temperatures. Higher intensity LED resulted in inhomogenous thermal behavior of the tested materials, especially of S.
Tài liệu tham khảo
M.S. Gale, and B.W. Darvell, “Thermal cycling procedures for laboratory testing of dental restorations,” Journal of Dentistry, vol. 27, pp. 89–99, 1999.
D.C. Palmer, M.T. Barco, and E.J. Billy,“Temperature extremes produced orally by hot and cold liquids,” Journal of Prosthetic Dentistry, vol. 67, pp. 325–7, 1992.
C.G. Plant, D.W. Jones, and B.W. Darvell, “The heat evolved and temperature attained during setting of restorative materials,” British Dental Journal, vol. 137, pp. 233–8, 1974.
L. Musanje, and B.W. Darvell, “Effects of strain rate and temperature on the mechanical properties of resin composites”, Dental Materials, vol. 20, pp. 750–65, 2004.
R.H. Bullard, K.F. Leinfelder, C.M. Russell, “Effect of coefficient of thermal expansion on microleakage”, Journal of American Dental Association, vol. 116, pp. 871–4, 1988
X. Henchang, L. Wenyi, W. Tong, “Measurement of thermal expansion coefficient of human teeth”, Australian Dentistry Journal, vol. 34, pp. 530–5, 1989.
P. Lambrechts, C. Ameye, G. Vanherle, „Conventional and microfilled composite resins. Part II: Chip fractures”, Journal of Prosthetic Dentistry, vol. 48, pp. 527–38, 1982.
J.M. Powers, R.W. Hostetler, J.B. Dennison, “Thermal expansion of composite resins and sealants”, Journal of Dental Research, vol. 58, pp. 584–7, 1979.
K.J.M. Soderholm, “Influence of silane treatment and filler fraction on thermal expansion of composite resins”, Journal of Dental Research, vol. 63, pp. 1321–6, 1984.
R. Yamaguchi, J.M. Powers, J.B. Dennison, “Thermal expansion of visible-light-cured composite resins”, Operative Dentistry, vol. 14, pp. 64–7, 1989.
A. Versluis, W.H. Douglas, R.L. Sakaguchi, “Thermal expansion coefficient of dental composites measured with strain gauges”, Dental Materials, vol. 12, pp. 290–4, 1996
W.H. Souder, and C.G. Peters, “An investigation of the physical properties of dental materials”, Dental Cosmos, vol. 62: pp. 305–12, 1920.
J.K. Park, B. Hur, C.C. Ko, F. Garcia-Godoy, H.I. Kim, Y.H. Kwon, “Effect of light-curing unit on the thermal expansion of resin nanocomposites”, American Journal of Dentistry, vol. 23, issue 6, pp. 331–334, 2010.
I. Sideridou, D. Achilias, E. Kyrikou, “Thermal expansion characteristics of light-cured dental resins and resin composites”, Biomaterials, vol 25, pp. 3087–97, 2004.
E.E. Rose, J. Lal, R. Green, J. Cornell, “Direct resin filling materials: coefficient of thermal expansion and water sorption of polymer methacrylate”, Journal of Dental Research, vol 34, pp 589–96, 1955.
A. Versluis, W.H. Douglas, R.L. Sakaguchi, “Thermal expansion coefficient of dental composites measured with strain gauges”, Dental Materials, vol 12, issue 5, pp. 290–4, 2005.
R. Nomoto, “Effect of light wavelength on polymerization of light-cured resins”, Dental Materials Journal, vol 16, issue 1, pp. 60–73, 1997.
F.A. Rueggeberg, W.F. Caughmann, J.W. Curtis Jr, “Effect of light intensity and exposure duration on cure of resin composite”, Operative Dentistry, vol 19, issue 1, pp. 26–32, 1994.
S. Jadhav, V. Hegde, G. Aher, N. Fajandar, “Influence of light curing units on failure of direct composite restorations”, Journal of Conservative Dentistry, vol. 14, issue 3, pp. 225–7, 2011.
C.S. Pfeifer, J.L. Ferracane, R.L. Sakaguchi, R.R. Braga, “Factors affecting photopolymerization stress in composites”, Journal of Dental Research, vol 87, issue 11, pp. 1043–7, 2008.
J.K. Park, B. Hur, C.C. Ko, F. Garcia-Godoy, H.I. Kim, Y.H. Kwon, “Effect of light-curing units on the thermal expansion of resin nanocomposites”, American Journal of Dentistry, vol 23, issue 6, pp. 331–334, 2010.
C.J. Baek, S.H. Hyun, S.K. Lee, H.Y. Seol, H. Kim, Y.H. Kwon, “The effects of light intensity and light-curing time on the degree of polymerization of dental composite resins”, Dental Materials, vol 27, issue 4, pp. 523–33, 2008.
V. Mucci, G. Arenas, R. Duchowicz, W.D. Cook, C. Vallo, C, “Influence of thermal expansion on shrinkage during photopolymerization of dental resins based on bis- GMA/TEGDMA”. Dental Materials, vol. 25, pp. 103–14, 2009.
S.K. Sidhu, T.E. Carrick, J.F. McCabe., “Temperature mediated coefficient of dimensional change of dental tooth- colored restorative materials”, Dental Materials, vol. 20, issue 5, pp. 435–40, 2004.
Y.G. Kim, S. Hirano, H. Tadashi, “Physical properties f resin-modified glass-ionomers”, Dental Materials Journal, vol. 17, issue 1, pp. 68–76, 1998
Z. Yan, S.K. Sidhu, T. Carrick, J.F. McCabe, “Response to thermal stimuli of glass ionomer cements”, Dental Materials, vol. 23, pp. 597–600, 2007.
W. Lien, and K.S. Vandewalle, “Physical properties of a new silorane-based restorative system”, Dental Materials, vol. 26, issue 4, pp. 337–44, 2010.
V. Miletic, V. Ivanovic, B. Dzeletovic, M. Lezaja, “Temperature changes in silorane-, ormocer-, and dimethacrylate-based composites and pulp chamber roof during ilght-curing”, Journal of Esthetic and Restorative Dentistry, vol. 21, pp. 122–32, 2009.
I. Nica, V. Rusu, N. Cimpoesu, P. Vizureanu, A. Aluculesei, [Thermal and structural properties of nano- and micro-filled composites]. Rev Med Chir Soc Med Nat Iasi, 1 vol. 13, issue 3, pp. 892–8, 2009.
M. Oliveira, P.F. Cesar, M. Giannini, F.A. Rueggeberg, J. Rodrigues, C.A. Arrais, “Effect of temperature on the degree of conversion and working time of dual-cured resin cements exposed to different curing conditions”, Operative Dentistry, vol. 37, issue 4, pp. 370–9, 2012.
A. Kishen, and A. Asundi, “Investigation of thermal property gradients in the human dentine, Journal of Biomedical Materials Research, vol 55, pp. 121–30, 2001