Dynamic fatigue of indented, soda-lime glass as a function of temperature
Tóm tắt
Dynamic fatigue data as a function of temperature for indented-annealed and indented-aged soda-lime glass was analysed using an exponential crack velocity equation based on stress corrosion theory. Agreement in the crack velocity parameters as derived from the two sets of data indicates that the residual contact stress of the indented-aged samples was properly accounted for. However, the predicted macroscopic crack velocity curves based on the indentation fatigue data did not agree with those based on double cantilever beam measurements and possible reasons are discussed.
Tài liệu tham khảo
S. W. Freiman, Fracture Mechanics of Glass, in “Glass Science and Technology”, Vol. 5, edited by D. R. Uhlmann and N. J. Kriedl (Academic Press, New York, 1980) pp. 21–78.
R. J. Charles andW. B. Hillig, The Kinetics of Glass Failure by Stress Corrosion, in “Symposium on Mechanical Strength of Glass and Ways of Improving It”, Florence, Italy, 25–29 September (1961) (Union Scientifique Continentale de Verre, Charleroi, Belgium, 1962) pp. 511–27.
S. M. Wiederhorn andL. H. Bolz,J. Amer. Ceram. Soc. 53 (1970) 543.
S. W. Wiederhorn, Mechanics of Subcritical Crack Growth in Glass, in “Fracture Mechanics of Ceramics”, Vol. 4, edited by R. C. Bradt, D. P. H. Hasselman, and F. F. Lange (Plenum Press, New York, 1978) pp. 549–80.
S. M. Wiederhorn, E. R. Fuller Jr andR. Thomson,Metal Sci. 14 (1980) 450.
D. B. Marshall andB. R. Lawn,J. Amer. Ceram. Soc. 63 (1980) 532.
B. R. Lawn, D. B. Marshall, G. R. Anstis andT. P. Dabbs,J. Mater. Sci. 17 (1982) 1108.
T. P. Dabbs, B. R. Lawn, andP. L. Kelly,Phys. Chem. Glasses 23 (1982) 58.
D. K. Shetty, A. R. Rosenfeld, P. McGuide, G. K. Bansal andW. H. Duckworth,Amer. Ceram. Soc. Bull. 59 (1980) 1193.
G. G. Trantina,J. Amer. Ceram. Soc. 62 (1979) 377.
J. E. Ritter, M. Vicedomine, K. Breder andK. Jakus,ibid. 67 (1984) 198.
J. E. Ritter Jr, N. Bandyopadhyay andK. Jakus,Amer. Ceram. Soc. Bull. 60 (1981) 798.
K. Jakus, J. E. Ritter Jr andJ. M. Sullivan,J. Amer. Ceram. Soc. 64 (1981) 372.