Characterization of artificially patinated layers on artistic bronze exposed to laboratory SO2 contamination
Tóm tắt
Artificially patinated artistic bronze was exposed to the action of 0.10 and 12.68 ppm SO2 contamination in the laboratory at 100% relative humidity. The surface layers were characterized using electrochemical, atomic absorption, X-ray powder diffraction techniques and Fourier transform–infrared spectrometry. Thermal and calorimetric studies were also performed. Some of the compounds identified were cuprite (Cu2O), digenite (Cu1.8S), yarrowite (Cu9S8), chalcocite (Cu2S), brochantite (Cu4(OH)6SO4), bonattite (CuSO4·3H2O) and Sn2S3.
Tài liệu tham khảo
T. E. GRAEDEL, K. NASSAU and J. P. FRANEY, Corros. Sci., 27 (1987) 639.
G. BRUNORO, G. GILLI and R. NAGLIATI, Surf. Technol. 21 (1984) 125.
E. MATTSSON and R. HOLM, “Metal Corrosion in the Atmosphere”, ASTM STP 435 (American Society for Testing and Materials, Philadelphia, PA, 1968) p. 187.
N. HJELM-HANSEN, Stud. Conserv. 29 (1984) 17.
K. NASSAU, P. K. GALLAGHER, A. E. MILLER and T. E. GRAEDEL, Corros. Sci. 27 (1987) 669.
K. NASSAU, A. E. MILLER and T. E. GRAEDEL, ibid. 27 (1987) 703.
J. M. BASTIDAS, M. P. ALONSO, E. M. MORA and B. CHICO, Werkst. Korros. 45 (1995) 515.
E. OTERO, J. M. BASTIDAS, W. LOPEZ and J. L. G. FIERRO, ibid. 45 (1994) 387.
R. B. COMIZZOLI, J. P. FRANEY, T. E. GRAEDEL, G. W. KAMMLOTT, A. E. MILLER, A. J. MULLER, G. A. PEINS, L. A. PSOTA-KELTY, J. D. SINCLAIR and R. C. WETZEL, J. Electrochem. Soc. 139 (1992) 2058.
J. M. BASTIDAS and J. SIMANCAS, Characterization of Corrosion Products on a copper-containing intrauterine device during storage at room temperature. Submitted to Biomaterials1996.
M. LENGLET, K. KARTOUNI and D. DELAHAYE, J. Appl. Electrochem. 21 (1991) 697.
C. FIAUD and N. GHIMOUZ, Br. Corros. J. 24 (1989) 279.
J. VEDEL and M. SOUBEYRAND, J. Electrochem. Soc. 127 (1980) 1730.
R. L. DEUTSCHER and R. WOODS, J. Appl. Electrochem. 16 (1986) 413.
U. R. EVANS, “Metallic Corrosion Passivity and Protection” (E. Arnold, London, 1948) p. 64.
H. LANGFEKDEROVÁ, M. LINKESOVÁ, M. SERATOR and J. GAZO, J. Thermal Anal. 17 (1979) 107.
H. KADAMA, “Infrared Spectra of Minerals”, 1st edn (Minister of Supply and Services, Ottawa, Ontario, Canada, 1985).
E. DELTOMBE, N. DE ZOUBOV, C. VANLEUGENHAGHE and M. POURBAIX, “Atlas of Electrochemical Equilibria in Aqueous Solutions” (Pergamon, London, 1966) p. 475.
S. E. KHALAFALLA and I. D. SHAH, Metall. Trans. 1 (1970) 2151.
M. E. WADSWORTH, K. L. LEITER, W. H. PORTER and J. R. LEWIS, ibid. 218 (1960) 519.
J. R. LEWIS, J. H. HAMILTON, J. C. NIXON and C. L. GRAVERSEN, Trans. TMS-AIME(1948) 2388.