Study of microporosity formation in nickel-base superalloys
Tóm tắt
The susceptibility of nickel-base superalloys to microporosity formation is studied experimentally and theoretically. Analysis of a model introduced herein leads to formulation of a microporosity index, ΔP *, which is expressed in terms of solidification parameters and alloy system properties. This index can be determined from information obtained by quantitative differential thermal analysis. The effect of composition on the formation of microporosity is evaluated. Thus, aluminum, titanium, and cobalt are found to increase, and chromium to decrease microporosity. The effect of carbon is beneficial or detrimental depending on the aluminum content in the alloy.
Từ khóa
Tài liệu tham khảo
S. Rupp, Y. Bienvenu, and J. Massol: Rapport final-actions concertées COST 50-III, Novembre 84, Ecole des Mines, Paris.
J. Lecomte-Beckers:Metall. Trans. A, 1988, vol. 19A, pp.
J. Lecomte-Beckers and M. Lamberigts:Proc. of High Temperature Alloys for Gas Turbine and Other Applications 1986, D. Reidel Publ. Co., Dordrecht, The Netherlands, 1986, vol. I, pp. 745–57.
H. Fredriksson and G. Rogberg:Metal Science, Dec. 1979, pp. 685–90.
M.C. Flemings:Solidification Processing, Materials Science and Engineering Series, McGraw-Hill, New York, NY, 1974.
R. Mehrabian, M. Keane, and M. C. Flemings:Metall. Trans., 1970, vol. 1, p. 1209.
D. Apelian, M. C. Flemings, and R. Mehrabian:Metall. Trans., 1974, vol. 5, p. 2533.
H. Fredriksson and I. Svensson:Metall. Trans. B, 1976, vol. 7B, p. 599.
J. Campbell:The British Foundryman, April 1969, p. 147.
T.Z. Kattamis and M.C. Flemings:Trans. TMS-A1ME, 1967, vol. 239, pp. 1504–11.
N. Streat and F. Weinberg:Metall. Trans. A, 1976, vol. 7A, pp. 417–23.